1) Re-Mg compacted graphite cast iron
稀土镁蠕铁
1.
In this paper, the best technique of the isothermal quenching is obtained from the result of quite cross experiment, to increare the strenglh and toughness of the Re-Mg compacted graphite cast iron, on the basis of the C-curve of it.
本文在作者测定的稀土镁蠕铁C—曲线的基础上,经正交设计,优选出稀土镁蠕铁等温淬火的最佳工艺,使蠕铁的强韧性成倍提高。
2) rare earth Mg ductile iron
稀土镁球铁
1.
The possibility of using rare earth Mg ductile iron to replace steel 10 was expounded.
分析了10钢制耐火砖成型模板过早失效的形式及原因,论证了采用稀土镁球铁代替10钢制作成型模板的可行性。
3) Re-Mg ductife iron
稀土镁铸铁
1.
The preparation,value assignment and the application of the Re-Mg ductife iron CRM was systematically studied.
对稀土镁铸铁光谱分析用标准物质的制备、分析定值及应用进行了系统研究。
4) rare earth austenite bainite compacted graphite cast iron
稀土奥-贝蠕铁
5) rare earth-magnesium nodular cast iron
稀土镁球墨铸铁
1.
Development of certified reference materials for spectrometric analysis of rare earth-magnesium nodular cast iron;
稀土镁球墨铸铁光谱分析用标准物质的研制
6) Si-Mg-Fe alloy
稀土硅镁铁合金
1.
The measurement of Ti content in Si-Mg-Fe alloy by diantipyrylmethane photometric method;
二安替比林甲烷光度法测定钛在稀土硅镁铁合金的应用
补充资料：镁稀土锆系铸造镁合金
镁稀土锆系铸造镁合金
magnesium-rare earth- zirconium cast magnesium alloy series
me.x一tugaoxi zhuzao me一hejin镁稀土错系铸造镁合金(magnesiumrareearth一zireonium east magnesium alloy series) 以稀土、错为主要合金化元素的铸造镁合金，高温性能良好，亦称耐热铸造镁合金。该系合金由于在20。~300℃时具有高的强度和抗蠕变性能而受到重视。属于该系合金的中国牌号有ZM一3(o.2%一0.7%Zn，2·5%~4·o%RE，0.5%一1.0%Zr，Mg为余量)，ZM一4(2 .0%一3.0%Zn，2.5%一4.0%RE，0.5%一1.0%Zr，Mg为余量)，ZM一6(0.2%一0.7%Zn，2.0%一2·8%Nd，o·4%一1·o%Zr，Mg为余量)等合金。合金中起热强作用的为稀土元素，随稀土含量的增加合金的强度及耐热性显著提高，但塑性则不断下降;加入足够数量的错能使其晶粒度显著细化，提高合金的室温和高温力学性能，并改善铸造性能;该系合金还有少量的锌，其主要作用是降低合金的线收缩和表面缩陷的倾向。 镁稀土错系铸造镁合金的显微组织特征是由固溶体和分布在晶界上的块状化合物组成。合金在固溶处理人工时效状态下，具有良好的室温和高温力学性能其力学性能见表1。表1镁稀土错系铸造镁合金力学性能二六 镁稀土错系铸造镁合金有较小的结晶温度间隔，而且它们的共晶体有很好的流动性，良好的铸造性能，其缩松、热裂的倾向小，充型能力好，可用于铸造形状复杂和要求气密性的铸件。其铸造工艺性能及物理常数见表2。 表2镁稀土错系铸造镁合金铸造 工艺性能及物理常数襄傀·粼罐不纂纂霍嘿肠翼