1) coking behaviour
炼焦性质
1.
The coking behaviours of coal samples after benzene extraction were almost totally destroyed.
对6种煤用苯在加压下抽提出沥青后,发现煤的炼焦性质几乎完全破坏。
2) coking coal qualities
炼焦煤性质
1.
The paper represent the influence of coking coal qualities for coke thermal property by using types of Xuangang coal through experimental study.
选用宣钢常用的炼焦煤种,实验研究炼焦煤性质对焦炭热性能的影响,基本确定了炼焦煤灰、硫、挥发分、黏结指数、煤的最大胶质厚度与焦炭热性能的相关关系,对合理开发应用炼焦煤资源,有针对性的优化配煤结构、提高焦炭热性能,具有很好的指导作用。
4) coking applicability
炼焦适用性
5) scorch safety
混炼焦烧性能
1.
The scorch time t s and dynamic curing index Δ t during mixing in a wider range of temperatures (110～160 ℃) and rotor speeds (40～100 r·min -1 ) on Brabender torque rheometer and the Mooney scorch safety ( t 5 and Δ t 30 ) were measured by using CR mix prepared on an open mill.
根据试验数据 ,拟合了CR的混炼焦烧性能与混炼温度或转子转速的关系及关系模型 ,从橡胶力化学反应的角度解释了温度和转子转速对CR混炼焦烧性能的影响趋势 ,并在此基础上对该模型进行了验证。
6) mixing scorch safety
混炼焦烧特性
1.
The mixing scorch safety ( t s and Δ t ) of four kinds of rubber compounds (NR,SBR,BR and NBR) was measured using a Brabender torque rheometer in a wide temperature range (100～140 ℃) and rotor speed range (20～80 rpm),and compared to Mooney scorch safety ( t 5 and Δ t 30 ).
采用Brabender转矩流变仪 ,在混炼温度为 10 0～ 14 0℃和混炼转子转速为 2 0～ 80r·min- 1 的条件下测试了4个胶种 (NR ,SBR ,BR和NBR)的混炼焦烧特性 (ts 和Δt) ,并与门尼焦烧特性 (t5和Δt30 )进行比较 ,指出门尼焦烧不能真正地反映混炼胶在实际加工过程中的焦烧特性。
补充资料：捣固炼焦
扩大炼焦煤源的炼焦方法之一。利用专门的捣固机械，将装炉煤料捣固成煤饼，然后从炭化室的一侧推入。使装炉煤料的堆密度可以增大到0.95吨/米3以上（顶装焦炉煤料堆密度一般为 0.75吨／米3左右）。捣固炼焦，对采用以胶质层厚度在11～14毫米的气煤为主的煤料，效果比较显著。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。