1.
On the basis of orthogonal experiment, the effect of Mg content and heat treatment on mechanical properties of near eutectic Al Si cast alloys modified with Sr has been investigated.
以正交试验为基础 ,通过调整Mg含量和热处理工艺 ,分析它们对Sr变质近共晶Al Si铸造合金力学性能的影响。
2.
The effect of carbon content on element segregation and corrosion resistance of the cast alloy Fe 30Ni 20Cr 6Mo has been investigated.
研究了Ｆｅ－３０Ｎｉ－２０Ｃｒ－６Ｍｏ铸造合金中微量元素Ｃ对合金元素偏析和耐蚀性的影响。
3.
Effect of microstructure and element distribution of an iron base cast alloy Cr30Nil7Mo2Cu solidified at different rates upon the erosion-corrosion behaviour in flowing suspension of solid particles in strong acidic medium has been investigated by metallograph, XRD, EPMA and hardness tests.
用扫描电镜、Ｘ射线衍射、电子探针等手段测定及分析了Ｆｅ基铸造合金Ｃｒ３０Ｎｉ１７Ｍｏ２Ｃｕ以不同速度凝固后的显微组织和主要合金元素分布，在含固相颗粒的强酸性双相流介质中测定了冲刷腐蚀性能。
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条