1) non-distortion welding
动态控制焊接变形
3) dynamical controlled low stress no-distortion welding
动态低应力无变形焊接
4) monitor welding deformation
监控焊接变形
1.
It also explained the technique to monitor welding deformation under free status, with the shims to realize the four studs spiral progression rim plate piling, to adopt different size of tight bolts and heaters to heat up the rim plates to reach the expected expanding capacity, to put s.
采用了自由状态下监控焊接变形;加填隙片,旨在呈4头螺旋线型堆叠磁轭冲片;采用了不同规格的压紧螺杆;又采用管状电阻加热棒加热磁轭,致使达到应有的膨胀量,加装垫片为预紧量,使磁轭热套于圆盘式结构支架上;并采用了多种组合键调整控制联结等新结构、新工艺、新技术和新标准。
5) solder joint shape control
焊点形态控制
1.
By using this concept a novel BGA interconnection technology, named as induction heating reflow, is developed with detailed discussions of size effect of induction heat, reflow processing parameters, thermal characteristics, solder joint shape control and interfacial reactions.
为了解决无铅面阵封装整体加热引发的可靠性问题,本文引入了局部选择性加热的概念,利用这一概念开发高频感应加热重熔微电子面阵封装与组装互连新方法,并分别从感应加热尺寸效应、焊接工艺、热特性,焊点形态控制以及界面反应等方面展开讨论。
6) dynamic control low stress no distortion
动态控制低应力无变形
补充资料：焊接变形
焊接变形
distortion in weldments
hanjle blanxing 焊接变形(distortion in weldments)全属 焊接时或焊接后，由于不均匀加热和不均匀冷却引起 的金属焊接结构的变形。焊接变形大致可分为8类: (l)纵向收缩变形。构件焊后在焊缝方向发生收缩，如 图1中的△乙。(2)横向收缩变形。构件焊后在垂直焊缝 方向发生收缩，如图1中的△召。(3)弯曲变形(图2)。 构件焊后发生弯曲。弯曲可由焊缝的纵向收缩引起，也 可由焊缝横向收缩引起。(4)角变形(图3)。焊后构件堰票到{副}渠囊到+目{ 图1纵向和横向收缩变形的平面围绕焊缝产生的角位移。(5)波浪变形(图4)。焊后构件呈波浪形，在薄板焊接时最容易发生。(6)错边变形(图5)。在焊接过程中，两焊接件的热膨胀不一致，可能引起长度方向上的错边和厚度方向上的错边。(7)扭转变形(图6)。焊后在结构上出现的扭曲。(8)张开变形(图7)。平板对接时，焊炬前方出现张开现象。一窿白一‘ 之立童鱼宝 b 图2弯曲变形 a一焊缝纵向收缩引起;b一焊缝横向收缩引起 一甲 图3角变形处遥乡、气蛋建乡 图4波浪变形业久二多酬 ab 图5错边变形 a一无点固泌一有点固 霆葬冀霎 图6扭转变形巨弓 图7张开变形