1) MoS_2-LaF_3cosputtered film
MoS_2-LaF_3
2) MoS2
MoS_2
1.
MoS2 powders coated with Ni are successfully prepared via Ni (NO3) 2 decomposition-hydrogen reduction, then added to Ni-Cr25 (wt% ) alloy powders to produce solid self-lubricating composites of Ni-Cr25(wt% ) alloy by vacuum hot pressing at 1 050℃ and 10 MPa.
添加Ni包覆MoS_2粉末,Ni-Cr25(w％)高温固体自润滑材料的机械性能优于未包覆材料,对(MoS_2/Ni)20w％的高温固体自润滑材料的摩擦磨损性能分析表明:在室温和600℃下,材料有较低的摩擦系数,室温磨损率也很低,在高温下与未添加包覆材料相比前者具有很好的宽温带摩擦学性能。
2.
Bonded coatings are made by super fine powder MoS2 and graphite that can resist high temperature and reduce friction.
利用MoS_2超细粉+石墨制作的粘结涂层,涂层耐一定高温,减摩效果好。
3.
Tribolpgical characteristics and wear failure mechanism of bonded solid lubricant (MoS2) film used on YL12 aluminum alloy - 45# steel frictional pair were studied systematically.
本文系统考察了以MoS_2为固体润滑剂的有机粘结固体润滑涂层润滑YL12铝合金-45#钢磨擦副时的摩擦学性能及其在铝合金表面的失效机理。
3) tribological proformence
DDP/LaF_3
4) MoS2/Ti3SiC2
MoS_2/Ti_3SiC_2
1.
The MoS2/Ti3SiC2 multilayer materials were prepared by multistep that pre-synthesized Ti3SiC2 powders are used to prepare multilayer materials.
研究了采用分步法制备MoS_2/Ti_3SiC_2层状复合材料的工艺,其制备过程分2步进行。
5) MoS_2 films
MoS_2膜
6) SrF2LaF3 system
SrF_2-LaF_3系
补充资料：glistening object of LaF3:Ce
分子式：
CAS号：
性质：掺Ce3+的LaF3闪烁体的一些特性非常类似于CeF3。密度介于BaF2和BGO间，它的主要衰减时间是26.5ns，但还有一个3ns快的和一个185ns慢的成分。这两成分随Ge3+浓度减少而增加。因LaF3:Ce发射峰主要在约300nm处，需采用石英或UV玻璃窗口光电倍增管，适用于现代医学图像显示技术等。