1) impregnation density
浸渍密度增量
3) impregnation sealant
浸渍密封
1.
A kind of heat-resistant material-polyimide was chosen as impregnation sealant,and the proper impregnating and solidifying methods were used,through which the graphite rings could be efficiently impregnated twice and after solidifying, polyimide was obtained with heat-resistance (obvious heat-degradation was not observed at 450℃).
选择耐高温的高分子材料———聚酰亚胺作为浸渍密封剂，采用二次真空、加压浸渍工艺和适当的固化方法，既能使聚酰胺酸有效地浸渍石墨环，又能使固化后得到的聚酰亚胺具有最佳耐高温性（在４５０℃没有明显的热解现象）。
4) impregnation increment
浸渍量
1.
Through a study on the cunninghamia lanceolata veneer impregnation increment for wind turbine blades used composite materials, the impregnation effects were evaluated, a conclusion with regard to the relationship between impregnation increment and time was drawn.
通过对风力发电机叶片复合材料杉木单板树脂浸渍量的研究,正确评估杉木单板的浸渍效果,得出杉木单板的浸渍量与浸渍时间的关系。
2.
The impregnation increment of epoxy resin for carbonized bamboo board with conventional impregnation is low.
采用常规浸渍的方法,炭化竹板的环氧树脂浸渍量低。
3.
In order to explore the epoxy resin impregnation property of the raw and semifinished materials of wind turbine blades composite materials-carbonized bamboo sheet and Cunninghamia lanceolata thin timber,the relationship between their resin impregnation increment and impregnation time was studied.
为了探索风力发电机叶片复合材料原材料炭化竹片及杉木薄板的环氧树脂浸渍性能,将炭化竹片及杉木薄板浸渍在不同固含量的混合环氧树脂中,研究炭化竹片及杉木薄板试件在不同浸渍时间的浸渍量。