2) barium titanate powder
![点击朗读](/dictall/images/read.gif)
钛酸钡粉体
1.
Qualitative analysis of tetragonal barium titanate powder was discussed from the result of X-ray diffraction experiment by testing the standard series samples.
通过对标准试样进行X射线衍射(XRD)测试,根据衍射峰的积分强度、衍射角及d值等数据对超细钛酸钡粉体四方相的含量进行了定量分析,本文的研究发现衍射角较衍射峰强度的数据有相对的稳定性,根据两峰衍射角之差来分析四方相含量比较准确,从而为由水热法制备的四方相钛酸钡粉体四方相含量的表征提供了一种简单的分析手段。
2.
High purity barium titanate powder without barium carbonate was prepared by hydrothermal method at 240℃,in 6 hours, using BaCl_2·2H_2O and TiCl_4·NaOH was a mineralizer and the ratio between Ba~2+ and Ti~4+ is 3.
采用BaCl2 TiCl4 NaOH系统,通过水热反应合成了高纯钛酸钡粉体,提出了以[NaOH]/[TiCl4]作为衡量反应体系碱度的标准,通过精确测量pH值,在[NaOH]/[TiCl4]=10,Ba/Ti=3。
3) strontium titanate powders
![点击朗读](/dictall/images/read.gif)
钛酸锶粉末
4) magnesium titanate powder
![点击朗读](/dictall/images/read.gif)
钛酸镁粉末
1.
The technology of general synthesizing electric ceramic powder is used to make magnesium titanate powder.
本文采用常规的电子陶瓷粉末合成工艺制备了钛酸镁粉末 ,研究了原材料纯度、合成保温时间对产品电性能的影响。
6) bismuth barium titanate powder
![点击朗读](/dictall/images/read.gif)
钛酸铋钡粉体
补充资料:低温钛酸钡系热敏陶瓷
分子式: BaTiO3
CAS号:
性质:居里温度120℃以下的热敏陶瓷。除主成分钛酸钡外,还含锶、铝、钇、硅等氧化物。材料常温电阻率低,一般为10~102Ω·cm,升阻比(电阻落差)大,为103~108,耐压特性高,电压特性低。电极采用化镀镍或铜后,表面再镀银或烧银方法制成,也可直接烧渗银锌制成欧姆接触电极。主要用于制作彩电消磁、马达启动、过流保护等元件。
CAS号:
性质:居里温度120℃以下的热敏陶瓷。除主成分钛酸钡外,还含锶、铝、钇、硅等氧化物。材料常温电阻率低,一般为10~102Ω·cm,升阻比(电阻落差)大,为103~108,耐压特性高,电压特性低。电极采用化镀镍或铜后,表面再镀银或烧银方法制成,也可直接烧渗银锌制成欧姆接触电极。主要用于制作彩电消磁、马达启动、过流保护等元件。