In combination with the results of stress corrosion cracking(SCC)tests,it is proposed that fatiguecrack growth for this steel in foregoing aqueoussolutions is controlled mainly by oxygen de-polarization reactions(ODR)rather than by hydrogen embrittlement(HE)mechanism unless cathodicpolarization result.
5%Nacl 和10%NH_4NO_3水溶液中的疲劳裂纹扩展速率(FCGR)及外加极化电位的影响进行了实验研究,结合应力腐蚀(SCC)实验,作者认为,除非在阴极极化条件下出现强烈充氢情况,该钢在中性水溶液中的麦劳裂纹扩展主要受氧去极化作用(ODR)控制而不是氢脆(HE)机制。
3) oxygen depolarization corrosion
氧去极化腐蚀
4) oxygen depolarization control
氧去极化控制
5) oxygen depolarized reaction
氧去极化反应
1.
The corrosion mechanism is oxygen depolarized reaction, and the corrosion exhibits Fe and Pb lost pit corrosion, and also has features of general corrosion.
5%NaCl溶液中具有良好的耐腐蚀性能;腐蚀机理为氧去极化反应,表现为脱铁、脱铅的点蚀形态,同时具有全面腐蚀的特征;腐蚀产物主要有三类,一类是与Fe元素有关的腐蚀产物,另一类则与Pb有关的腐蚀产物,还有一类是Cu的氧化物;ZCuSn3Zn8Pb6Ni1FeCo合金中的δ-Cu10Sn3具有较强的耐腐蚀能力。
6) oxygen cathode
氧去极化阴极(oxygen depolarization cathode)
补充资料：氧去极化控制
分子式：
CAS号：
性质：当腐蚀过程的阴极反应是溶液中溶解氧的还原反应时，腐蚀速度主要为阴极氧去极化的极化程度所决定，这类腐蚀过程称为氧去极化控制。大多数金属在中性和碱性溶液中以及少数正电性金属在含有溶解氧的弱酸性溶液中的腐蚀都属于此类控制。在这种情况下，由于作为腐蚀的去极化剂是氧分子，故阴极过程分为两个基本环节：氧向金属表面的输送过程和氧离子化反应过程。如果阴极过程在不大的电流密度下进行，且阴极表面氧的供应充足，则阴极过程的速度由氧离子化过电位控制(oxygen ionizing overvoltage control)。此时，阴极氧的过电位与电流密度成线性关系。由于氧的溶解度小，在溶液中的浓度很低，如果在较大的电流密度下进行，则阴极过程的速度主要由氧向金属表面输送、通过静止层(又称扩散层)的扩散步骤所控制称为氧扩散控制(oxygen diffusion control)。
CAS号：
性质：当腐蚀过程的阴极反应是溶液中溶解氧的还原反应时，腐蚀速度主要为阴极氧去极化的极化程度所决定，这类腐蚀过程称为氧去极化控制。大多数金属在中性和碱性溶液中以及少数正电性金属在含有溶解氧的弱酸性溶液中的腐蚀都属于此类控制。在这种情况下，由于作为腐蚀的去极化剂是氧分子，故阴极过程分为两个基本环节：氧向金属表面的输送过程和氧离子化反应过程。如果阴极过程在不大的电流密度下进行，且阴极表面氧的供应充足，则阴极过程的速度由氧离子化过电位控制(oxygen ionizing overvoltage control)。此时，阴极氧的过电位与电流密度成线性关系。由于氧的溶解度小，在溶液中的浓度很低，如果在较大的电流密度下进行，则阴极过程的速度主要由氧向金属表面输送、通过静止层(又称扩散层)的扩散步骤所控制称为氧扩散控制(oxygen diffusion control)。