1) Critical treatment
临界处理
2) sub-critical treatment
亚临界处理
1.
A study on hardening behavior for high chromium cast iron 16Cr2MolCu under sub-critical treatment;
16Cr2Mo1Cu高铬铸铁在亚临界处理中硬化行为研究
2.
This paper mainly studied the transformation of microstructure and change of properties of high chromium alloy (HCA) grinding balls for cement mills subjected to sub-critical treatment, and analyzed the hardening mechanism by using X-ray diffraction, SEM,magnetism method and hardness test.
主要研究了水泥磨机用高铬磨球采用亚临界处理工艺时的组织转变和性能的变化,并用X衍射、扫描电镜、磁性法和硬度测定法分析了它的硬化机制。
3.
The sub-critical treatment process for this cast iron was discussed.
测试了含钨高铬耐磨铸铁经不同工艺亚临界处理后的硬度,探讨了含钨高铬耐磨铸铁亚临界处理工艺。
3) subcritical treatment
亚临界热处理
1.
The Influence of the quenching and tempering treatment and the different subcritical treatment on microstrcture and property of a high alloy white cast iron was studied.
研究了淬回火和不同的亚临界热处理工艺对高合金白口铸铁组织和性能的影响。
2.
After subcritical treatment,the tensile strength of the sample slightly decreases.
经过亚临界热处理后,试样的抗拉强度有所下降,但冲击韧度有了很大的提高。
4) sub-critical treatment
亚临界热处理
1.
The hardening behavior and abrasion resistance of high chromium cast iron(HCCI) containing molybdenum and vanadium subjected to sub-critical treatment were studied.
研究表明,通过亚临界热处理可以使含有大量残留奥氏体的高铬铸铁产生二次硬化,从而提高高铬铸铁的硬度和耐磨性。
2.
The effect of Mo and Cu on the solidification structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied in this paper.
研究了Mo和Cu对高铬铸铁凝固组织和亚临界热处理硬化行为的影响。
5) sub-critical heat treatment
亚临界热处理
1.
Study on the sub-critical heat treatment of 16Cr-2.5Mn high chromium white iron;
16Cr-2.5Mn高铬白口铁的亚临界热处理研究
2.
The results show that the wear resistance is improved due to austenite transforming into martensite after sub-critical heat treatment.
研究了高铬白口铸铁亚临界热处理后耐磨性和显微组织的关系。
6) intercritical heat treatment
临界区热处理
1.
In this paper,the microstructure and properties of 35CrMo steel after intercritical heat treatment of various temperatures have been studied and the effects of IHT on the cryogenic toughness were discussed.
研究了３５ＣｒＭｏ钢经不同温度临界区热处理后的显微组织与性能，并着重探讨了对其低温韧性的影响，试验结果得出：３５ＣｒＭｏ钢经临界区淬火并４７０℃中温回火后，与常规热处理态在保持等强度的同时，低温韧性有明显提高，－２０℃的冲击值提高８０％。
补充资料：表面处理、热处理关连用语英汉对照
age hardening 时效硬化 ageing 老化处理
air hardening 气体硬化 air patenting 空气韧化
annealing 退火 anode effect 阳极效应
anodizing 阳极氧化处理 atomloy treatment 阿托木洛伊表面
austempering 奥氏体等温淬火 austenite 奥斯田体/奥氏体
bainite 贝氏体 banded structure 条纹状组织
barrel plating 滚镀 barrel tumbling 滚筒打光
blackening 染黑法 blue shortness 青熟脆性
bonderizing 磷酸盐皮膜处理 box annealing 箱型退火
box carburizing 封箱渗碳 bright electroplating 辉面电镀
bright heat treatment 光辉热处理 bypass heat treatment 旁路热处理
carbide 炭化物 carburized case depth 浸碳硬化深层
carburizing 渗碳 cementite 炭化铁
chemical plating 化学电镀 chemical vapor deposition 化学蒸镀
coarsening 结晶粒粗大化 coating 涂布被覆
cold shortness 低温脆性 comemtite 渗碳体
controlled atmosphere 大气热处理 corner effect 锐角效应
creeping discharge 蠕缓放电 decarburization 脱碳处理
decarburizing 脱碳退火 depth of hardening 硬化深层
diffusion 扩散 diffusion annealing 扩散退火
electrolytic hardening 电解淬火 embossing 压花
etching 表面蚀刻 ferrite 肥粒铁
first stage annealing 第一段退火 flame hardening 火焰硬化
flame treatment 火焰处理 full annealing 完全退火
gaseous cyaniding 气体氧化法 globular cementite 球状炭化铁
grain size 结晶粒度 granolite treatment 磷酸溶液热处理
graphitizing 石墨退火 hardenability 硬化性
hardenability curve 硬化性曲线 hardening 硬化
heat treatment 热处理 hot bath quenching 热浴淬火
hot dipping 热浸镀 induction hardening 高周波硬化
ion carbonitriding 离子渗碳氮化 ion carburizing 离子渗碳处理
ion plating 离子电镀 isothermal annealing 等温退火
liquid honing 液体喷砂法 low temperature annealing 低温退火
malleablizing 可锻化退火 martempering 麻回火处理
martensite 马氏体/硬化铁炭
metallikon 金属喷镀法
metallizing 真空涂膜 nitriding 氮化处理 ~
nitrocarburizing 软氮化 normalizing 正常化
oil quenching 油淬化 overageing 过老化
overheating 过热 pearlite 针尖组织
phosphating 磷酸盐皮膜处理 physical vapor deposition 物理蒸镀
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条
|