1) modified hexahydric resin
改性六羟树脂
1.
Classical synthesis process of modified hexahydric resin is improved: methylolation is changed from at atmospheric pressure into at a negative pressure, a reasonable material ratio is determined, methanol is used as etherifying agent, methylolation temperature is 65～68℃, etherification temperature 63～65℃.
对改性六羟树脂的经典合成工艺进行了改进:将羟甲基化反应由常压改为在一定的负压下进行,确定了合理的物料配比,选用甲醇作醚化剂,羟甲基化反应温度为65～68℃,醚化反应温度为63～65℃。
2) hexa-hydroxy resin
六羟树脂
3) modified resin
改性树脂
1.
The preparation of the modified resin and its demulsification mechanism in the treatment of emulsified oil wastewater were investigated.
采用季铵盐改性树脂工艺处理模拟含乳化油废水,探讨了改性树脂的制备及其在含乳化油废水处理过程中的破乳机理。
2.
A conductive and heating coating of parallel circuit was developed using compound carbon-fillers such as graphite, carbon black, petroleum coke, graphite fiber, carbon fiber and SiC powders and modified resin by mechanical mixing and heating curing.
采用复合型炭系填料石墨、炭黑、煅烧石油焦、石墨纤维、炭纤维和碳化硅粉末等与合成改性树脂经机械混合及不等温固化,制得并联导电发热涂料;利用扫描电镜、伏安法体积电阻率测试仪和电参数测定仪对涂层进行测试分析。
3.
This agent consists of HG modified resin, cross linking agent, and HS solid particles.
该高温暂堵剂由HG改性树脂、交联剂、HS固相颗粒组成。
5) Modification of SAN Resin
SAN树脂改性
6) modified MF resin
改性MF树脂
补充资料：羟甲基尼龙改性栓醛树脂
分子式：
CAS号：
性质：是由羟甲基尼龙、苯酚、甲醛为主要原料，用酸或碱作催化剂，经缩聚、脱水制得热塑性或热固性酚醛树脂。尼龙，科学名称应为聚酰胺，羟甲基尼龙应是羟甲基聚酰胺。该树脂保持了一般酚醛树脂的优点、羟甲基尼龙的加入，改善了树脂的流动性，（热固性树脂黏度0.06～0.1Pa·s）提高了酚醛塑料的冲击强度和弯曲强度。该树脂适于制作快速成型（凝胶时间70～100s/150℃）的玻璃纤维增强塑料，制品机械强度高、耐热、耐磨。热塑性树脂可作上光剂，涂在印刷品、纸制品、皮革等表面，增强其韧性、耐磨性、光滑度等。
CAS号：
性质：是由羟甲基尼龙、苯酚、甲醛为主要原料，用酸或碱作催化剂，经缩聚、脱水制得热塑性或热固性酚醛树脂。尼龙，科学名称应为聚酰胺，羟甲基尼龙应是羟甲基聚酰胺。该树脂保持了一般酚醛树脂的优点、羟甲基尼龙的加入，改善了树脂的流动性，（热固性树脂黏度0.06～0.1Pa·s）提高了酚醛塑料的冲击强度和弯曲强度。该树脂适于制作快速成型（凝胶时间70～100s/150℃）的玻璃纤维增强塑料，制品机械强度高、耐热、耐磨。热塑性树脂可作上光剂，涂在印刷品、纸制品、皮革等表面，增强其韧性、耐磨性、光滑度等。