2) electroless Ni-P alloy
化学镀Ni-P合金
1.
Present research status of process of electroless Ni-P alloy plating on magnesium alloys is reviewed in this paper,including zinc immersion and direct electroless Ni-P alloy.
综述了镁合金化学镀Ni-P合金工艺的研究现状,包括浸锌法、直接化学镀Ni-P合金,主要集中在化学镀Ni-P合金主盐的选择,添加剂的研究以及组合镀层的研究等。
4) Electroless Plating Ni-P alloy
化学镀Ni-P合金
1.
The results showed that corrosion resistance of Q235 steel in HCl,H 2SO 4,NaOH solution were increased after electroless plating Ni-P alloy.
结果表明 ,化学镀Ni-P合金可以显著提高Q2 35钢在盐酸、硫酸和氢氧化钠溶液中的耐蚀
5) Ni-Co-P alloy coaling
Ni-Co-P合金镀层
6) electroless Ni-Co-W-P plating
化学镀Ni-Co-W-P
1.
In order to improve the deposition rate, anti - corrosion properties and high hydrogen overpotential of electroless Ni-Co-W-P plating, the effects of the composition, pH value, temperature, rotation speed and surface active agents were respectively studied on the deposition rate and corrosion resistance of electroless Ni-Co-W-P coating.
为改善化学镀Ni-Co-W-P合金工艺镀速慢、镀层耐腐蚀性能差、析氢过电位高等问题,研究了镀液组分、pH值、温度、转速、表面活性剂对45钢上化学镀Ni-Co-W-P合金镀层沉积速度、耐腐蚀性能、镀层厚度、孔蚀率、表面形貌和硬度的影响,得出最佳镀液配方:6g/LCoSO4,24g/LNiSO4,20g/LNaH2PO2,20g/LNa2WO4·2H2O,20g/L(NH4)2SO4,24g/LNa3C6H5O7,11g/L苹果酸,pH值7。
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)