2) waste expanded polystyrene(WEPS)
废泡沫聚苯乙烯
3) waste polystyrene foam
废聚苯乙烯泡沫塑料
1.
The process of recycling the waste polystyrene foam was investigated by means of solution grafting copolymerization ,as well as the effects of the amount of initiator, reaction temperature , concentration and type of monomer, multimonomer grafting copolymerization on the grafting rate and efficiency .
用溶液接枝的方法研究了回收的废聚苯乙烯泡沫塑料的接枝工艺 ,包括引发剂的用量、反应温度、单体浓度、单体种类、多单体共接枝对废聚苯乙烯泡沫塑料接枝的影响。
4) waste foamed polystyrene
废聚苯乙烯泡沫塑料
1.
Anti-freezing adhesive produced by waste foamed polystyrene;
废聚苯乙烯泡沫塑料制取抗冻胶粘剂
2.
An antifreezing adhesive of low toxicity,low cost and superperformance can be prepared from waste foamed polystyrene (used as a principal raw material)via solvent dissolution and modification.
以废聚苯乙烯泡沫塑料为主要原料 ,经溶剂消泡、改性后可制得低毒性的、粘接强度高的、低成本的改性抗冻胶粘剂。
5) waste polystyrene foam plastics
废弃聚苯乙烯泡沫塑料
1.
First, dissolve waste polystyrene foam plastics in the solvent ethyl acetate, making out macromolecule colloid.
利用对环境构成危害的废弃聚苯乙烯泡沫塑料为原料 ,以无毒、无公害的乙酸乙酯为溶剂 ,溶解后制成高分子胶粘液 ,向该胶粘液中加入表面活性剂十二烷基苯磺酸钠、增塑剂邻苯二甲酸二丁酯和遮盖剂 ,经球磨机研磨制成修正液。
6) waste polystyrene foam plastic
废聚苯乙烯泡沫塑料
1.
The paper introduces the method to produce modified adhesives by waste polystyrene foam plastic.
本文研究了废聚苯乙烯泡沫塑料制备改性胶粘剂的方法,并对其低毒混合溶剂、增粘树脂、改性剂和填料等进行优选,制得低毒性、低成本、高性能的胶粘剂。
补充资料：聚苯乙烯
| 聚苯乙烯 polystyrene 苯乙烯的聚合物。英文缩写PS。结构为  玻璃化温度80～90℃，非晶态密度1.04～ 1.06克／厘米3，晶体密度1.11～1.12克／厘米3，熔融温度240℃，电阻率为1020～1022欧·厘米。导热系数0.116瓦／米·开（ 30℃ ）。通常的聚苯乙烯为非晶态无规聚合物，具有优良的绝热、绝缘和透明性，长期使用温度0～70 ℃，但脆，低温易开裂。此外还有全同和间同立构聚苯乙烯。全同聚合物有高度结晶性。苯乙烯可由自由基、负离子、正离子及配位负离子机理聚合。聚合方法有本体、溶液、悬浮和乳液聚合。当聚合温度低于 100℃ 时，在很宽的转化率范围均可得到高分子量产品。加入 5％～25％乙苯的溶液聚合有利于传热，并改进产品性能，在工业上常用。乳液聚合易于控制聚合温度，转化率高，产物分子量高，但不易加工，残留分散剂影响聚合物性能。配位聚合可得到立体规整聚合物。 聚苯乙烯主要用于包装材料、建筑材料、电器、汽车零件、管材、仪表、生活用品及玩具等。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。