1) sintered iron based alloy
烧结铁合金
2) sintered steel
铁基烧结合金
1.
Effects of annealing and adding Si on the microstructure of M10 type sintered steel;
高温退火和添加Si对仿M10铁基烧结合金显微组织的影响
3) iron based alloy sintered at low temperature
低温烧结铁基合金
4) sintered NdFeB permanent alloy
烧结钕铁硼永磁合金
5) sintered alloy
烧结合金
1.
A newcomposite──carbon fiber fabric reinforced SiC/Cc-sintered alloy was developed.
为改善碳／碳复合材料的高温抗氧化性能，在碳布／液体酚醛中引入超细碳化硅（α－ＳｉＣ）粉进行复合，并在高纯氮气保护下高温烧结，初步制成了碳布增强ＳｉＣ／Ｃ共烧结合金材料。
2.
The high temperature wearability and the mechanism of wearing-resistance of carbon fiber reinforced SiC/phenolic aldehyde sintered alloy were studied and discussed.
对碳纤维增强ＳｉＣ／酚醛树脂烧结合金的高温耐磨性能及其耐磨机理进行了详细研究。
3.
First a carbon fiber reinforced SiC / C co-sintered alloy with high strength, high modulus and high temperature wearability was obtainted.
在高纯包气保护下进行高温烧结，首次获得了具有高强高模及高温耐磨性能的碳纤维增强ＳｉＣ／Ｃ共烧结合金。
6) co-sintered alloy
共烧结合金
补充资料：烧结铁
分子式：
CAS号：
性质：用粉末冶金方法制得的铁或铁基材料。常用原料为还原铁粉、电解铁粉和羰基铁粉，在（40～70）Pa的压力下压制成形，然后在氨分解气氛或发生炉煤气的保护下加热至1100～1300℃进行烧结。为了改善加工性能，在加热前常在700～900℃温度下进行退火处理。制品的拉伸强度为0.25～0.3GPa，延伸率为10%左右。为了提高烧结铁的致密度和力学性能，常在铁粉中加入少量硼、磷等元素。主要用作冶炼特种钢、精密合金、磁性材料等的添加剂或原料，也可作特殊用途的铁制品。
CAS号：
性质：用粉末冶金方法制得的铁或铁基材料。常用原料为还原铁粉、电解铁粉和羰基铁粉，在（40～70）Pa的压力下压制成形，然后在氨分解气氛或发生炉煤气的保护下加热至1100～1300℃进行烧结。为了改善加工性能，在加热前常在700～900℃温度下进行退火处理。制品的拉伸强度为0.25～0.3GPa，延伸率为10%左右。为了提高烧结铁的致密度和力学性能，常在铁粉中加入少量硼、磷等元素。主要用作冶炼特种钢、精密合金、磁性材料等的添加剂或原料，也可作特殊用途的铁制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。