3) toughened nylon
增韧尼龙
1.
The injection moulding and moist curing of toughened nylon shuttle used for loom were discribed in detail.
阐述了增韧尼龙织布梭的注射成型工艺及调湿处理工艺 ,分析了注塑过程中常见缺陷及其产生的原因 ,提出了解决问题的对策以及成型中的注意事
2.
Methods of maleic anhydride grafted EPDM (MAH-g-EPDM) and polyolefin elastomer(POE) toughened nylon were studied.
研究了用马来酸酐接枝EPDM和POE等聚烯烃增韧尼龙的方法 ,通过改变聚烯烃与尼龙的用量找出较佳的配比范围及实验方案。
4) glass fiber reinforced PA66
玻纤增强尼龙66
1.
The effects of red phosphorus flame-retardant masterbatch on the flame-retardant properties of glass fiber reinforced PA66 were investigated.
研究红磷阻燃母粒对玻纤增强尼龙66(PA66)阻燃性能的影响。
2.
In an attempt to overcome the drawbacks of direct application of red phosphorous in glass fiber reinforced PA66,the preparation technology of red phosphorous-based microcapsule fire retardant by in-situ polymerization was studied.
为克服红磷直接应用于玻纤增强尼龙66中的缺点,研究了用原位聚合法制备微胶囊红磷的工艺,测试了样品的吸湿性以及表面包覆性能,并研究了其用于玻纤增强尼龙66的阻燃性能和力学性能。
6) Polyamide(PA-66)
尼龙-66(PA-66)
补充资料：超韧尼龙
分子式：
CAS号：
性质：一类具有很高冲击韧性的尼龙。其特点是在干态时冲击强度比普通尼龙高十倍以上，低温时的冲击强度要高数倍以上，同时还保留尼龙的特性。通常由尼龙与接枝改性聚烯烃共混制造。具代表性的品种是ZYTELST-801，其拉伸强度53MPa，相对密度1.09，弯曲强度68.8MPa，悬臂梁冲击强度(缺口)87kJ/m，热变形温度71℃。由三元乙丙橡胶接枝马来酸酐(EPDM-g-MAH)与尼龙66共混制得。加工方法和用途与普通尼龙相近，特别适合制造需低温冲击韧性好的制品。
CAS号：
性质：一类具有很高冲击韧性的尼龙。其特点是在干态时冲击强度比普通尼龙高十倍以上，低温时的冲击强度要高数倍以上，同时还保留尼龙的特性。通常由尼龙与接枝改性聚烯烃共混制造。具代表性的品种是ZYTELST-801，其拉伸强度53MPa，相对密度1.09，弯曲强度68.8MPa，悬臂梁冲击强度(缺口)87kJ/m，热变形温度71℃。由三元乙丙橡胶接枝马来酸酐(EPDM-g-MAH)与尼龙66共混制得。加工方法和用途与普通尼龙相近，特别适合制造需低温冲击韧性好的制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。