1) Alkaline earth stannates
碱土锡酸盐
2) alkaline earth aluminate
碱土铝酸盐
1.
Current research progress in alkaline earth aluminate-based persistent phosphorescent materials doped by rare earth ions are reviewed in this paper.
系统地分析和概括了稀土离子激活碱土铝酸盐体系长余辉发光材料的种类、特性、组成、结构、发光机理和制备技术,并根据长余辉发光材料研究现状,探讨了碱土铝酸盐长余辉发光材料的研究方向与发展前景。
2.
A luminescent plastics was prepared by adding zinc sulfide(ZnS) or alkaline earth aluminate luminescent pigments in polyproplene.
分别将ZnS类发光颜料及碱土铝酸盐类发光颜料加入到聚丙烯中,制成ZnS发光塑料和碱土铝酸盐发光塑料,测定其辉度、余辉时间及光稳定性。
3) alkaline earth aluminates
碱土铝酸盐
1.
We make research on acryric acid emulsion based luminescence coating by adding the mix of alkaline earth aluminates and rare earth elements.
采用稀土元素掺杂的碱土铝酸盐光致发光材料研制丙烯酸乳液型发光涂料。
2.
Post-treating process, combined gel-coating and surface-film coating routes, for alkaline earth aluminates long after-glow phosphors was studied.
采用胶体包覆和表面成膜包覆相结合的方法,对碱土铝酸盐蓄光型发光材料进行包覆后处理研究。
5) chlorosilicate
碱土氯硅酸盐
1.
Alkali earth chlorosilicate of Sr8Si4O12Cl8:(Eu3+,M3+)(M=Bi3+,Gd3+)was synthesized by the high temperature solid state method and using Na2CO3 as charge compensation agent.
以Na2CO3为电荷补偿剂,采用高温固相法合成了碱土氯硅酸盐Sr8Si4O12Cl8:(Eu3+,M3+)(M=Bi3+,Gd3+)荧光材料。
2.
The alkali earth chlorosilicate of Sr8Si4O12Cl8∶Eu3+,M3+(M=Sm3+,Al3+)was synthesized by the high temperature solid state method.
采用高温固相法合成了碱土氯硅酸盐Sr8Si4O12Cl8∶Eu3+,M3+(M=Sm3+,Al3+)发光材料,并通过激发光谱和发射光谱的测试,首次在碱土氯硅酸盐体系中研究了Sm3+、Al3+三价金属离子对Eu3+发光性能的影响及其相对发光强度随组成变化的规律。
补充资料：锡酸
化学式H2SnO3。有两种形态:α锡酸和β锡酸。它们都是二氧化锡的水合物,其通式为xSnO2·y H2O。α锡酸长期放置或加热会逐渐变成β锡酸。α 锡酸常称氢氧化锡(Ⅳ)，为白色无定形固体或凝胶状沉淀,难溶于水,溶于酸、碱：
α 锡酸可由锡(Ⅳ)盐或四卤化锡在室温下水解，或与适量碱或氨水作用而得：
这里的Sn(OH)4就是H2SnO3·H2O，也是SnO2·2H2O。
β锡酸为白色细晶固体,具有SnO2四方晶体结构,不溶于水、酸和碱。在稀的酸或碱作用下会发生胶溶作用而形成溶胶。
经X射线研究证明,这两种锡酸都是含水的锡石SnO2，并不是两种异构体。它们的溶解性不同是由于粒子大小和聚结程度的不同造成的。
α 锡酸可由锡(Ⅳ)盐或四卤化锡在室温下水解，或与适量碱或氨水作用而得：
这里的Sn(OH)4就是H2SnO3·H2O，也是SnO2·2H2O。
β锡酸为白色细晶固体,具有SnO2四方晶体结构,不溶于水、酸和碱。在稀的酸或碱作用下会发生胶溶作用而形成溶胶。
经X射线研究证明,这两种锡酸都是含水的锡石SnO2，并不是两种异构体。它们的溶解性不同是由于粒子大小和聚结程度的不同造成的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条