1) Self-cross linked latex
自交联胶乳
2) self crosslinking em ulsion
自交联乳液
1.
The resultsshow ed thata proper thickness ofthe interm ediate of the core shellself crosslinking em ulsion w as needed in order toobtain the optim um film properties.
研究了乳胶粒组成对含有环氧基、氨基和羧基的多层核壳型室温自交联乳液的涂膜性能。
3) non-formaldehyde self-cross-linking acrylic emulsion
无醛自交联乳液
4) self-crosslinked silicone-acrylate emulsion
自交联硅丙乳液
1.
Polymerization technology of self-crosslinked silicone-acrylate emulsion with high-organosilicone content pre-pared by reactive emulsifier was studied.
研究了以反应性乳化剂制备高硅含量自交联硅丙乳液的聚合工艺,结果表明:以反应性乳化剂代替普通乳化剂,采用后交联技术结合种子乳液法,分步控温,并加入丙二醇作为水解抑制剂,可以显著提高自交联硅丙乳液的聚合稳定性,获得高硅含量的自交联硅丙乳液。
5) self-crosslinking polyacrylate emulsion
自交联纯丙乳液
1.
The combination of silicone emulsion and self-crosslinking polyacrylate emulsion was used as a binder for preparing a kind of water-borne ultra thin intumescent fire retardant coating for steel structure.
采用聚有机硅氧烷乳液与自交联纯丙乳液的混合乳液为基料,制备了水性超薄膨胀型钢结构防火涂料,并研究了聚合物基料对其性能的影响。
6) Ambient temperature self crosslinking
室温自交联乳液
补充资料:自交联丙烯酸树脂
分子式:
CAS号:
性质:成膜时聚合物链之间能自行交联成网状结构的丙烯酸树脂。经自交联的丙烯酸树脂可明显改善耐水性和耐溶剂性,机械强度和耐热性也有提高。但交联度过高,将使膜硬脆,手感变差。丙烯酸系单体和两种含不同官能基(如羟基、羧基和氨基等)的单体或一种含两类官能基的单体(如羟甲基丙烯酰胺,含羟基和氨基)共聚所得的溶液聚合物或乳液聚合物,成膜时聚合物链上的两类官能基相互反应而实现自交联。也可用多价金属作自交联剂。为使官能基间相互反应,成膜温度应高于官能基发生反应的温度。自交联丙烯酸乳液树脂主要用作织物、皮革、纸张处理剂;自交联丙烯酸溶液树脂主要用作涂料。
CAS号:
性质:成膜时聚合物链之间能自行交联成网状结构的丙烯酸树脂。经自交联的丙烯酸树脂可明显改善耐水性和耐溶剂性,机械强度和耐热性也有提高。但交联度过高,将使膜硬脆,手感变差。丙烯酸系单体和两种含不同官能基(如羟基、羧基和氨基等)的单体或一种含两类官能基的单体(如羟甲基丙烯酰胺,含羟基和氨基)共聚所得的溶液聚合物或乳液聚合物,成膜时聚合物链上的两类官能基相互反应而实现自交联。也可用多价金属作自交联剂。为使官能基间相互反应,成膜温度应高于官能基发生反应的温度。自交联丙烯酸乳液树脂主要用作织物、皮革、纸张处理剂;自交联丙烯酸溶液树脂主要用作涂料。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。