1) decorating firing time
烤烧时间
2) baking time
烘烤时间
1.
The present paper discusses the effect of baking temperature、baking time and pre-strain on the bake hardenability of ultra low carbon bake hardening steel(ULC-BH steel).
研究分析烘烤温度、烘烤时间、预应变量等烘烤条件对超低碳烘烤硬化钢烘烤硬化性能的影响。
3) baking time
焙烤时间
5) sintering time
烧结时间
1.
Effect of sintering time on the performance of LiNi_xMn_(2-x)O-coated LiCoO_2;
烧结时间对LiNi_xMn_(2-x)O_4表面修饰LiCoO_2性能的影响
2.
It is found sintering temperature and sintering time have small effect on the composition of crystalline phase, but have great effect on the morphology of glass ceramics; When sintering temperature is above crystalline temperature, the effect on the size of crystal is greater.
以硼泥为主要原料对制备玻璃陶瓷工艺进行研究,实验中发现烧结温度和烧结时间对析晶相的成分影响较小,但玻璃陶瓷的表面形貌影响较大;当烧结温度高于析晶温度时,对晶体尺寸影响更大;根据不同烧结温度和烧结时间对玻璃陶瓷结构影响,找出适合的最佳烧结温度和烧结时间,其值为781℃,时间为4h。
3.
Effects of sintering time and crystallizing time on the microstructure of glass ceramic were also analyzed.
以硼泥为主要原料制备微晶玻璃,通过DTA, XRD, SEM等分析方法,对CaO-MgO-Al2O3-SiO2系玻璃的析晶性能进行研究,系统地分析了烧结时间和晶化时间对微晶玻璃结构的影响。
6) calcinations time
焙烧时间
1.
The performance for NO_x selective catalytic reduction under the conditions of different calcinations time, calcinations temperature, O_2 concentration and space velocity was studied.
并对焙烧温度和焙烧时间等不同制备条件和反应温度、O2 浓度和空速等不同反应条件下NOx 的选择性催化还原性能进行了研究 。
补充资料：焦烧时间
分子式：
CAS号：
性质：橡胶硫化反应的速度由零加速至反应明确出现为止所经历的时间，生产上也称焦烧时间。在这一阶段先由促进剂体系和硫黄生成促进剂多硫化合物，由它引发橡胶分子链产生可进一步交联的自由基。硫化诱导期主要取决于胶料配方，尤其是所选用的促进剂体系。此外，胶料在加工过程中所经受的热历程也是影响其诱导期的重要因素。
CAS号：
性质：橡胶硫化反应的速度由零加速至反应明确出现为止所经历的时间，生产上也称焦烧时间。在这一阶段先由促进剂体系和硫黄生成促进剂多硫化合物，由它引发橡胶分子链产生可进一步交联的自由基。硫化诱导期主要取决于胶料配方，尤其是所选用的促进剂体系。此外，胶料在加工过程中所经受的热历程也是影响其诱导期的重要因素。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。