1) nitrate coprecipitation
硝酸盐共沉淀
1.
10) were prepared by solid-state mixture and nitrate coprecipitation mixture.
用固态配料和硝酸盐共沉淀配料制备了各组份为(Bi_(1。
2) co-precipitating with nitrate
硝酸盐共沉淀法
1.
Result showed that: the catalyst prepared by co-precipitating with nitrate showed better catalytic performance and texture than that prepared by ammonia method.
研究结果表明,用硝酸盐共沉淀法制备的催化剂,其性能和结构均优于用蒸氨法制备的催化剂。
3) oxalate coprecipitation method
草酸盐共沉淀法
1.
BaTiO3 powder was synthesized by oxalate coprecipitation method,and through the experiment and characterizations of XRD,DTA-TG,IR,TEM the result indicated that the product BaTiO3 was cube,well-proportioned and the size was about 30nm and reunited less.
利用草酸盐共沉淀法合成BaTiO3纳米粉体,通过XRD分析、DTA-TG分析、IR分析及TEM形貌分析等分析手段,对制得的粉体进行了表征和测试,结果表明合成的BaTiO3粉体为单纯的立方相,粒径均匀,颗粒大小在30 nm左右,无严重的团聚现象。
2.
In order to develop more effective,nontoxic and environment-friendly inorganic luminescent nanomaterials for manifesting fingerprint,the Eu3 + doped LaPO4 nano-materials were synthesized by oxalate coprecipitation method.
为了研究新型高效的、对人体无毒、对环境无污染的显现指印的无机纳米荧光材料,采用草酸盐共沉淀法制备纳米发光材料LaPO4∶Eu3+,并利用PAMAM树形分子配置LaPO4∶Eu3+/PAM-AM G5。
4) carbonate co-precipitation
碳酸盐共沉淀法
1.
LiNi1/3Co1/3Mn1/3O2 was prepared by a carbonate co-precipitation method combined with an ultrasonic technique, followed by a high temperature solid state reaction.
在碳酸盐共沉淀法中引入超声波技术,合成锂镍钴锰前驱体,然后通过高温煅烧制备了LiNi1/3Co1/3Mn1/3O2正极材料,采用扫描电镜(SEM)、X射线能谱(EDS)、X射线衍射(XRD)、差示量热扫描(DSC)、循环伏安法(CV)及充放电测试等手段对材料进行了表征。
2.
LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 was prepared by a carbonate co-precipitation methode combined with a ultrasonic technique,followed by a high temperature solid state reaction,and the effec.
具体结论如下: 在碳酸盐共沉淀法中引入超声波技术合成锂镍钴锰氧正极材料,采用X射线衍射法(XRD)、扫描电镜法(SEM)、循环伏安法(CV)和充放电测试等手段,对材料进行表征与电化学性能研究。
5) carbonate co-precipitation method
碳酸盐共沉淀法
1.
The layered cathode materials LiNi1/3Co1/3Mn1/3O2 for Li-ion battery were synthesized by high temperature solid-state method,sol-gel method and carbonate co-precipitation method,respectively.
采用高温固相法、溶胶-凝胶法和碳酸盐共沉淀法分别制备了锂离子电池层状正极材料LiNi1/3Co1/3Mn1/3O2。
2.
Firstly, preparation of Li[Ni_(1/3)Co_(1/3)Mn_(1/3)]O_2 cathode material by carbonate co-precipitation method was studied via thermo gravimetry analysis(TG) of carbonate co-precipitation precursor, and X-ray diffraction(XRD) analy.
本论文首先研究了制备高密度球形Li[Ni_(1/3)Co_(1/3)Mn_(1/3)]O_2正极材料的一种新方法——碳酸盐共沉淀法。
3.
6) ferrite micropowder was prepared by carbonate co-precipitation method from metal sulfate solution using ammonium bicarbonate as precipitant.
以硫酸亚铁、硫酸锰和硫酸锌为原料,采用碳酸盐共沉淀法制备了Mn1–xZnxFe2O4(x=0,0。
6) Carbonate co-precipitation
碳酸盐共沉淀
1.
A series of spherical cathode material—LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 was synthesized by carbonate co-precipitation method and then examined by TG-DTA、ICP、XRD、SEM etc.
本文采用碳酸盐共沉淀法成功合成了球形LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2正极材料,同时采用TG-DTA、ICP、XRD、SEM、模拟电池测试等多种测试手段对该体系的制备与结构、形貌、性能做了系统的研究。
补充资料：共晶共沉淀
分子式：
CAS号：
性质：共沉淀法之一，指无法结晶的微量物质与常量物质产生共结晶沉淀而被载带出来。