1) Fe-Ni-P alloy coating
Fe-Ni-P合金镀层
1.
Study on internal stress of Fe-Ni-P alloy coating;
Fe-Ni-P合金镀层内应力研究
2) Ni-Fe-P coating
Ni-Fe-P镀层
3) Ni-Fe-W alloy coatings
Ni-Fe-W合金镀层
1.
A new Ni-Fe-W alloy coatings were obtained by pulse electrodeposition,the effect of W in the electrolyte contents on the structure of coatings,and the effect of the electrolyte contents on the hardness and thickness of coatings were discussed.
利用脉冲电沉积的方法制备了Ni-Fe-W合金镀层,讨论了镀液中W的含量对Ni-Fe-W合金镀层组织结构的影响,以及镀液成分对镀层硬度及厚度的影响。
2.
Then,the effects of the concentration of NiSO_4·6H_2O、Na_2WO_4·2H_2O、FeSO_4·7H_2O and temperature on the quality of Ni-Fe-W alloy coatings are also addressed.
并采用正交实验的方法研究了主盐浓度以及温度对脉冲电沉积Ni-Fe-W合金镀层的影响,通过对硬度、沉积速度以及外观的分析,筛选出了最佳的工艺条件。
4) Fe-Cr-Ni plating layer
Fe-Cr-Ni合金镀层
5) Ni-Fe alloy coatings
Ni-Fe合金镀层
1.
Bright Ni-Fe alloy coatings were prepared on 2024 aluminum alloy sheets from sulphate bath solution by electroplating.
采用电镀方法,在2024铝合金表面制备了光亮的Ni-Fe合金镀层。
2.
Ni-Fe alloy coatings with different electroplating time were prepared on 2024 aluminum alloy sheets by electroplating.
本文对这种方法进行了介绍,利用电镀法在2024铝合金上制备了不同电镀时间的Ni-Fe合金镀层,利用X射线ω扫描技术对镀层进行织构表征,对电镀时间与织构特性的关系进行了讨论。
6) Ni-Fe alloy coating
Ni-Fe合金镀层
1.
Annealing hardening of nanocrystalline Ni-Fe alloy coatings synthesized by brush plating using soluble anode
可溶性阳极电刷镀纳米晶Ni-Fe合金镀层的退火再强化
2.
Ni-Fe alloy coating was prepared on 2024 aluminum alloy sheets by electroplating.
利用电镀法在2024铝合金上制备了Ni-Fe合金镀层,随后对镀层在490℃进行2小时的退火处理。
补充资料：W-Ni-Fe alloy
分子式：
CAS号：
性质：一类重要的钨基重合金。它们是在钨中添加镍、铁而组成的合金，以及在这个基础上再加入其他金属元素的合金。加入的镍铁比一般为7：3或1：1。这类合金应用极广，已经成为用量最大的主要钨基重合金。其特点是烧结密度高，强度与塑性均较好，有一定的铁磁性。合金作为一般应用，如配重、平衡锤、防辐射屏蔽装置等，都直接使用烧结合金；但如作为要求高机械性能的应用时，合金则需变形加工及热处理以达到强化。
CAS号：
性质：一类重要的钨基重合金。它们是在钨中添加镍、铁而组成的合金，以及在这个基础上再加入其他金属元素的合金。加入的镍铁比一般为7：3或1：1。这类合金应用极广，已经成为用量最大的主要钨基重合金。其特点是烧结密度高，强度与塑性均较好，有一定的铁磁性。合金作为一般应用，如配重、平衡锤、防辐射屏蔽装置等，都直接使用烧结合金；但如作为要求高机械性能的应用时，合金则需变形加工及热处理以达到强化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。