1) Al-CoO System
Al-CoO体系
2) Cu_2O-Al system
Cu_2O-Al体系
1.
The results show that the chemical reaction of Cu_2O-Al system includes three different stages: in the first stage,there is a little reacted products of Al_2O_3 and Cu when temperature is lower than 910 K;in the second stage, chemical reaction doesn't occur in .
结果表明:Cu_2O-Al体系化学反应包括3个阶段,即第1阶段体系温度T<910 K,有少量Al_2O_3和Cu生成;第2阶段体系温度为910 K≤T<1103 K,Cu_2O-Al体系未发生化学反应;第3阶段体系温度为1103 K≤T≤1373 K,Cu_2O-Al体系发生化学反应,其产物为Cu、Al_2O_3及CuAlO_2。
3) O-Al system
O-Al体系
4) Al-Cr_2O_3 system
Al-Cr2O3体系
5) Al-K2ZrF6 system
Al-K2ZrF6体系
1.
A novel in-situ particulate reinforced aluminum matrix composite has been successfully developed by direct melt reaction(DMR) technique in the Al-K2ZrF6 system.
开发了Al-K2ZrF6体系熔体反应法合成原位铝基复合材料,采用XRD,SEM和TEM分析了复合材料中相组成、微观组织和界面结构。
6) Al-Pb system
Al-Pb体系
补充资料：silver-FeO-CoO2 material
分子式：
CAS号：
性质：银基含有氧化亚铁(FeO)和氧化钴(CoO2)的电接触材料。如Ag-6FeO-10CoO2的密度9.3～9.7g/cm3。布氏硬度784.0～1078.7MPa，电阻系数为2.80～3.30×10-2Ω·mm2/m。用粉末冶金方法制造。用作中等负荷电接触材料。
CAS号：
性质：银基含有氧化亚铁(FeO)和氧化钴(CoO2)的电接触材料。如Ag-6FeO-10CoO2的密度9.3～9.7g/cm3。布氏硬度784.0～1078.7MPa，电阻系数为2.80～3.30×10-2Ω·mm2/m。用粉末冶金方法制造。用作中等负荷电接触材料。