1) Model surface of Nb2O5
氧化铌模型表面
2) model of interfacial oxide
界面氧化层模型
3) surface oxidization
表面氧化
1.
The surface oxidization behaviors of Ce-5La(at%) alloy in dry air at 200 ℃ was investigated.
研究了Ce-5La(原子百分数)合金在200℃、干燥空气中的表面氧化反应行为。
2.
This paper macrographically analyzed the surface oxidization and the thichness of oxidized layer of 4004 alloy which successively undergo different temperature and different holding time during 350～525 ℃ according to the hot rolling bolding processes of 4004/3003/4004.
模拟４００４／３００３／４００４热轧复合工艺，对４００４合金在３５０～５２５℃分别加热保温所制备的试样表面氧化情况、氧化层厚度进行了宏观分析。
4) surface oxidation
表面氧化
1.
Enrichment of Cu,Ni in surface oxidation layer of copper-bearing age-hardening steel was investigated.
研究了Cu、Ni在含铜时效钢表面氧化层中的富集规律。
2.
In order to solve the problem that copper wire is oxidized easily,using the oxidation live-weight gain experiment,the surface oxidation of different structure and purity copper wires have been studied.
为了解决单晶铜线材在存储过程中的氧化问题,本文通过氧化增重实验,对不同组织、不同纯度铜线材的表面氧化行为进行了研究。
3.
Based on the Griffith theory, this paper suggested that the compressive strength of diamond can be enhanced by means of surface oxidation.
本文以Griffith微裂纹理论为基础,认为对金刚石晶体颗粒进行表面氧化处理,使表面微裂纹钝化或消除。
5) niobium oxide
氧化铌
1.
The new technique of preparing high pure-low fluorin niobium oxide from hydroxide niobium by extraction method was studied.
以氢氧化铌为原料,研究了萃取法制备高纯低氟氧化铌的新工艺,讨论了工艺条件对产品质量的影响,由正交试验得出较佳工艺条件为萃取剂和水比为11,萃取时间为20min,洗涤次数10次,煅烧温度800℃。
6) niobium monoxide
一氧化铌
补充资料：过氧化铌
分子式：HNbO4·nH2O
CAS号：
性质：又称过氧铌酸。黄色，不溶于水，室温时不溶于稀硫酸，和浓硫酸作用放出臭氧，和浓盐酸作用放出氯气。100℃；时完全分解，将氢氧化铌和30%浓度的过氧化氢作用或过铌酸钾和浓硫酸作用均可获得过氧化铌。
CAS号：
性质：又称过氧铌酸。黄色，不溶于水，室温时不溶于稀硫酸，和浓硫酸作用放出臭氧，和浓盐酸作用放出氯气。100℃；时完全分解，将氢氧化铌和30%浓度的过氧化氢作用或过铌酸钾和浓硫酸作用均可获得过氧化铌。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。