1) macrocell
氧浓差
1.
The behaviour and mechanism of the oxygen concentration difference macrocell were investigated for steel A3 in the 3.
结果表明，３种宏电池的作用规律相同，且随氧浓差异增大，宏电池效应系数也增大，这时宏电池中阳极金属的腐蚀显著加速。
2) oxygen concentration cell
氧浓差电池
1.
2O9 ceramics were investigated by means of ac impedance spectroscopy, oxygen concentration cell and oxygen pump (electrochemical oxygen permeation) at 600～1000 ℃ in various at- mospher.
结果表明,氧浓差电池电动势的实测值与理论值吻合得很好,氧离子迁移数为1,表明该陶瓷样品在该温度下氧气气氛中为一纯氧离子导体;氧泵(氧的电化学透过)实验结果进一步证实了该样品在氧气气氛中为一纯氧离子导体;在氧分压p(O2)=10-5～105Pa的高氧分压气氛中,电导率与氧分压变化基本无关,表明在该氧分压范围内样品为纯离子导体,这与氧浓差电池电动势测定结果相吻合;在低氧分压为10-5～10-15Pa范围内,总电导率随氧分压降低而稍有升高,表明在该氧分压范围样品为氧离子与电子的混合导体;在600～1000℃下氧离子电导率>10-2S?cm-1,显著高于母体La2Mo2O9的氧离子电导率,1000℃时的氧离子电导率为0。
2.
In the presence of SO_2, the EMF of the oxygen concentration cell increases, but the relation between EMF and ox.
还研究了氧化锆氧浓差电池的电动势受SO_2影响的情况,有SO_2存在时,氧浓差电池的电动势增大,但电动势与氧分压的关系不再符合Nernst公式。
3.
The ion conduction properties of the ceramic sample have been studied by impedance spectra,oxygen concentration cell,oxygen pump(electrochemical oxygen permeation) techniques in the temperature range of 600～1000 ℃.
采用交流阻抗谱、氧浓差电池、氧泵等电化学方法系统地研究了该陶瓷样品在600～1000℃下的离子导电特性。
3) macrocell corrosion
氧浓差腐蚀
4) Oxygen concentration cell
氧浓差电势
5) differential aeration cell corrosion
氧浓差电池腐蚀
6) concentration cell oxygen sensor
氧浓差电池型氧传感器
参考词条
补充资料：氧浓差电池腐蚀
分子式：
CAS号：
性质：同一金属的不同部位与含氧量不同的溶液相接触，形成氧浓差电池(又称充气不均匀电池)而导致的腐蚀。这是局部腐蚀的重要因素之一。例如，盛放中性介质的容器的水线腐蚀就是典型例子。由于水线(液面)处与空气接触，氧易到达，氧浓度高成为阴极区，而紧靠水线(液面)的下方部位，由于氧的浓度相对低而成为阳极区，最终导致容器中紧靠液面的周壁处发生严重的腐蚀。
CAS号：
性质：同一金属的不同部位与含氧量不同的溶液相接触，形成氧浓差电池(又称充气不均匀电池)而导致的腐蚀。这是局部腐蚀的重要因素之一。例如，盛放中性介质的容器的水线腐蚀就是典型例子。由于水线(液面)处与空气接触，氧易到达，氧浓度高成为阴极区，而紧靠水线(液面)的下方部位，由于氧的浓度相对低而成为阳极区，最终导致容器中紧靠液面的周壁处发生严重的腐蚀。