1) PWHT
焊后热处理(PWHT)
1.
THE NEW TRENDS OF PWHT;
焊后热处理（PWHT）的最新动向
2) post welding heat treatment
焊后热处理
1.
This study is concerned with the effect of post welding heat treatment(PWHT)on the microstructure and properties at the intercritical reheated coarse-grained heat-affected zone(IRCGHAZ)of WB36 steel, and investigated whether the PWHT could reduce IRCGHAZ embrittlement.
针对WB36钢(15NiCuMoNb5)临界再热粗晶区(IRCGHAZ)存在的脆化现象,研究了焊后热处理对模拟临界再热粗晶区(IRCGHAZ)组织性能的影响,探讨其改善韧性作用。
2.
This paper studies the technology,equipment and properties of post welding heat treatment of the RE microalloy quenching rail which was heated with medium frequency induction and quenched with pressure air for head of,normalized for other of.
通过热模拟试验选择了合理的焊后热处理工艺参数，恢复了轨头强度和硬度，并大幅度地提高了焊接接头的韧塑性和综合性能，满足了无缝线路铺设使用要求。
3.
It is pointed out that post welding heat treatment will not significantly improve residual stress in dissimilar steel welding joints unless correct and appropriate heat treatment procedures are taken.
文章主要讨论了焊接热处理对火电站管道异种钢焊接接头带来的问题,分析了热处理对接头组织、焊接残余应力的影响,指出通过焊后热处理可以明显改善电厂管道异种钢焊接接头残余应力,但要使用正确和合适的热处理工艺。
3) postweld heat treatment
焊后热处理
1.
Effect of postweld heat treatment on microstructure of electron beam welded joints of Ti_3Al;
焊后热处理对Ti_3Al电子束焊缝组织形态的影响
2.
Numerical value analysis on reduction of welding residual stresses with postweld heat treatment on P91 pipes;
焊后热处理消除P91钢管焊接残余应力的数值分析
3.
Based on Barkhausen Noise,as-welded residual stresses and residual stress after postweld heat treatment of 16MnR(include weld- ing metal,fusion zone,heat affect zone)were measured by using magneto-elastic method with 20～70 kHz frequency & 0.
07mm的STRESS- CAN500C磁弹性应力仪,测量了压力容器用16MnR钢焊后以及焊后热处理的残余应力(包括焊缝、熔合区、热影响区),研究了残余应力的形成、不同区域的分布。
4) Post weld heat treatment
焊后热处理
1.
The application and requirement of post weld heat treatment used by spherical tanks are summarized.
概述了球罐的应用及对焊后热处理的要求,详细介绍了国内球罐热处理技术的新进展,包括电加热法、爆炸法、内燃法、电加热辅助燃油法,还展望了该领域技术的发展前景。
2.
The influence of different post weld heat treatment conditions on the microstructures and mechanical properties of friction welded joints between drill pipe DZ60 steel and its tie in 40Cr steel has been discussed.
同时发现 ,采用合适的焊后回火热处理温度 ,可以有效提高焊接接头的抗拉强度及屈服强度 ,使其各项力学性能达到DZ6 0钻杆管材的技术标准 ,从而有效减少地质钻杆摩擦焊接头焊后热处理工艺 ,降低制造成
3.
The effect of post weld heat treatment on the impact toughness in inertia friction welded joints of carbon steel was studied in this paper The result show that the post weld heat treatment greatly affected the impact toughness of inertia friction welded joints The impact toughness of the welded joints can be improved by an adequate post weld heat treatmen
研究了焊后热处理对碳钢惯性摩擦焊接头冲击韧性的影响。
5) post-weld heat treatment
焊后热处理
1.
Effect of post-weld heat treatment on microstructure and mechanical property of manual SHS welding
焊后热处理对手工自蔓延焊接接头组织性能的影响
2.
The experiment results show that the welding defects can be decreased by using preheat and post-weld heat treatment.
试验表明 ,采取焊前预热 ,焊后热处理的TIG焊工艺进行焊接可以减少焊接缺陷的产生。
3.
Effects of post-weld heat treatment on the mechanical properties of Al-Li alloy 2091 joints are studied in this paper.
研究了2091铝锂合金焊后热处理对焊接接头机械性能的影响。
6) PWHT
焊后热处理
1.
Feasibility of canceling PWHT of Cr5Mo steel pipe with P5 electrode;
P5焊条焊接Cr5Mo钢管取消焊后热处理可行性研究
2.
MICROSTRUCTURE INVESTIGATION OF 12Cr1MoV STEEL SMALL DIAMETER TUBE JOINT CANCELING OUT POST WELDING HEAT TREATMENT(PWHT);
12Cr1MoV钢小直径管焊接接头取消焊后热处理的组织研究
3.
For the quality of product,we must control the rechecking of material,shell rolling,welding,NDT,PWHT very well to increase whole quality of the shell.
为了保证氨合成塔的制造质量,应加强对该设备从材料的检验、内筒卷制、焊接、探伤、焊后热处理等全过程的质量控制,从而提高筒体制造的整体质量。
补充资料：金属热处理:真空热处理
将金属工件在 1个大气压以下(即负压下)加热的金属热处理工艺。20世纪20年代末﹐随著电真空技术的发展﹐出现了真空热处理工艺﹐当时还仅用於退火和脱气。由於设备的限制﹐这种工艺较长时间未能获得大的进展。60～70年代﹐陆续研製成功气冷式真空热处理炉﹑冷壁真空油淬炉和真空加热高压气淬炉等﹐使真空热处理工艺得到了新的发展。在真空中进行渗碳﹐在真空中等离子场的作用下进行渗碳﹑渗氮或渗其他元素的技术进展﹐又使真空热处理进一步扩大了应用范围。
特点 金属零件在真空中的热处理能防止氧化脱碳并具有脱气效应﹐但金属元素可能蒸发。
防止氧化脱碳 真空热处理炉的加热室在工作时处於接近真空状态﹐仅存在微量一氧化碳和氢气等﹐它们对於加热的金属是还原性的﹐不发生氧化脱碳的反应﹔同时还能使已形成的氧化膜还原﹐因此加热后的金属工件表面可以保持原来的金属光泽和良好的表面性能。
脱气效应 金属零件在真空环境中加热时﹐金属中的有害气体﹐例如鈦合金中的氢和氧﹐会在高温下逸出﹐有利於提高金属的机械性能。
金属元素蒸发 各种元素都有自身的蒸气压﹐如果环境中的压力低於某种元素的蒸气压﹐这种元素就会蒸发。在真空热处理时﹐应根据钢中所含合金元素的蒸气压来选择加热时的真空度或温度﹐以避免合金元素蒸发。
工艺 真空热处理可用於退火﹑脱气﹑固溶热处理﹑淬火﹑回火和沉淀硬化等工艺。在通入适当介质后﹐也可用於化学热处理。
真空中的退火﹑脱气﹑固溶处理主要用於纯净程度或表面质量要求高的工件﹐如难熔金属的软化和去应力﹑不锈钢和镍基合金的固溶处理﹑鈦和鈦合金的脱气处理﹑软磁合金改善导磁率和矫顽力的退火﹐以及要求光亮的碳钢﹑低合金钢和铜等的光亮退火。真空中的淬火有气淬和液淬两种。气淬即将工件在真空加热后向冷却室中充以高纯度中性气体(如氮)进行冷却。适用於气淬的有高速钢和高碳高铬钢等马氏体临界冷却速度较低的材料。液淬是将工件在加热室中加热后﹐移至冷却室中充入高纯氮气并立即送入淬火油槽﹐快速冷却。如果需要高的表面质量﹐工件真空淬火和固溶热处理后的回火和沉淀硬化仍应在真空炉中进行。
特点 金属零件在真空中的热处理能防止氧化脱碳并具有脱气效应﹐但金属元素可能蒸发。
防止氧化脱碳 真空热处理炉的加热室在工作时处於接近真空状态﹐仅存在微量一氧化碳和氢气等﹐它们对於加热的金属是还原性的﹐不发生氧化脱碳的反应﹔同时还能使已形成的氧化膜还原﹐因此加热后的金属工件表面可以保持原来的金属光泽和良好的表面性能。
脱气效应 金属零件在真空环境中加热时﹐金属中的有害气体﹐例如鈦合金中的氢和氧﹐会在高温下逸出﹐有利於提高金属的机械性能。
金属元素蒸发 各种元素都有自身的蒸气压﹐如果环境中的压力低於某种元素的蒸气压﹐这种元素就会蒸发。在真空热处理时﹐应根据钢中所含合金元素的蒸气压来选择加热时的真空度或温度﹐以避免合金元素蒸发。
工艺 真空热处理可用於退火﹑脱气﹑固溶热处理﹑淬火﹑回火和沉淀硬化等工艺。在通入适当介质后﹐也可用於化学热处理。
真空中的退火﹑脱气﹑固溶处理主要用於纯净程度或表面质量要求高的工件﹐如难熔金属的软化和去应力﹑不锈钢和镍基合金的固溶处理﹑鈦和鈦合金的脱气处理﹑软磁合金改善导磁率和矫顽力的退火﹐以及要求光亮的碳钢﹑低合金钢和铜等的光亮退火。真空中的淬火有气淬和液淬两种。气淬即将工件在真空加热后向冷却室中充以高纯度中性气体(如氮)进行冷却。适用於气淬的有高速钢和高碳高铬钢等马氏体临界冷却速度较低的材料。液淬是将工件在加热室中加热后﹐移至冷却室中充入高纯氮气并立即送入淬火油槽﹐快速冷却。如果需要高的表面质量﹐工件真空淬火和固溶热处理后的回火和沉淀硬化仍应在真空炉中进行。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。