1) Fe-28Mn-4Si alloy
Fe-28Mn-4Si合金
1.
The microstructure of polycrystalline Fe-28Mn-4Si alloy was investigated by microscope and transmission electronic microscope.
以光学显微镜和透射电镜观察了Fe-28Mn-4Si合金的组织结构,并以弯曲法测定合金的形状记忆效应(SME)的大小,分析了多晶Fe-28Mn-4Si合金的组织结构及其与SME的关系。
2) Fe-15Mn-4Si-8Cr-4Ni shape memory alloy
Fe-15Mn-4Si-8Cr-4Ni形状记忆合金
1.
Effect of thermal-mechanical cycle training on corrosion resistance and low temperature relaxation of the Fe-15Mn-4Si-8Cr-4Ni shape memory alloy was studied,The results show that with the increase of the number of cycle,corrosion resistance of alloy in 5% NaOH solution decreases due to thermal-mechanical cycle treatment resulting in a large number of carbide precipitates.
研究了热-机械循环训练对Fe-15Mn-4Si-8Cr-4Ni形状记忆合金耐腐蚀性能以及低温松弛的影响,结果表明,随着循环次数的增加,合金在5%NaOH溶液中的耐腐蚀性能呈下降的趋势,这是因为热-机械循环处理导致了碳化物的大量析出,从而降低合金的耐腐蚀性能;经过热-机械循环处理后合金的低温应力松弛率高于未经循环处理的合金,约提高3%左右。
3) Pt-Fe alloy
Pt-Fe合金
4) Fe-B alloy
Fe-B合金
1.
Using WC,Cr3C2,Fe,Co and Ni as raw materials,and adding B element with the form of Fe-B alloy and agent PVB,the slurry for green body formation was prepared.
以Fe-B合金的形式在钢结硬质合金覆层配料中添加适量的元素B和有机粘结剂PVB,球磨混合后制备成料浆,喷涂在Q235钢基体上,通过真空液相烧结技术制备钢结硬质合金覆层材料。
2.
The preparation process, structure and magnetic properties of the electroless deposition Fe-B alloy film with rare earth joined were studied.
本文研究了化学沉积稀土Fe-B合金薄膜的制备工艺、组织结构和磁学性能。
3.
The influence of cooling rate and sample purity on non-equilibrium solidification of Fe-B alloy is researched by DSC technology.
采用DSC技术研究了Fe-B合金冷却速率及试样纯度对其非平衡凝固过程的影响,得到了不同实验条件下过冷度和转变分数的演化结果,并从经典形核理论、非等温结晶动力学等方面进行了分析和讨论。
5) Ti-Fe alloy
Ti-Fe合金
1.
Influence of composition on microstructure and properties of Ti-Fe alloys prepared by laser-induced self-propagating reaction synthesis;
成分对激光诱导自蔓延反应合成Ti-Fe合金组织性能影响
2.
Ti-Fe alloy nanometer powders with particle size between 5 nm~30 nm were prepared by gas evaporation with arc as a heating source.
实验结果表明,纳米粉末中化合物相的生成规律与Ti-Fe合金平衡相图的不同。
6) Fe-Ga alloy
Fe-Ga合金
1.
Microstructure and Magnetostrictive Properties of Melt-spun Fe-Ga Alloy Ribbons;
Fe-Ga合金薄带的显微组织及磁致伸缩性能
2.
A new magnetostrictive material of Fe-Ga alloy developed in recent years is introduced.
本文主要介绍了新型磁致伸缩材料Fe-Ga合金近几年的研究进展。
3.
The effect of Ga atom on the mean magnetic moment per atom of Fe-Ga alloys was discussed.
研究了Fe-Ga合金中Ga原子对合金的平均原子磁矩的影响。
补充资料：Fe-Si alloy
分子式：
CAS号：
性质：含硅0.5％～4.5％的铁硅合金。为硅在铁中的置换固溶体，属立方晶系。饱和磁感应强度为1.6～1.9J，铁损1～8W/kg。除了冲片使用外，常做成薄带，卷绕成铁芯。采用冷轧或进而热处理的方法获取结构(晶粒定向排列)。电力工业中用于电机、变压器等。电子工业中主要用于电源变压器、磁放大器等。
CAS号：
性质：含硅0.5％～4.5％的铁硅合金。为硅在铁中的置换固溶体，属立方晶系。饱和磁感应强度为1.6～1.9J，铁损1～8W/kg。除了冲片使用外，常做成薄带，卷绕成铁芯。采用冷轧或进而热处理的方法获取结构(晶粒定向排列)。电力工业中用于电机、变压器等。电子工业中主要用于电源变压器、磁放大器等。