1) Preirradiation graft copolymerization
预辐照接枝共聚
2) peroxidation preirradiation grafting copolymerization
预辐照共聚接枝
3) radiation inarch-copolymerize
辐照接枝共聚
4) preradiation grafting
预辐照接枝聚合
5) co-irradiated graft copolymerization
共辐照接枝
1.
The experiment proved that co-irradiated graft copolymerization can raise the two performances of high fiber,and the pre-irradiated graft copolymerization can raise adhesion strength only,but to heat-resistant it had no obvious effect.
实验证明,共辐照接枝法可同时提高纤维的两种性能,预辐照接枝则只能提高纤维的粘接性能,对提高其耐热性能无明显作用。
6) pre-irradiation grafting
预辐照接枝
1.
Polystyrene-divinylbenze-acrylonitrile(SDBAN)resin was synthesized by γ pre-irradiation grafting reaction and mutual radiation graftin reaction with acry lonitrile.
苯环有共轭π结构,它的π电子是非定域的,辐射时苯基吸收的能量虽然足以使键断裂,但由于能量很快在整个分子重新分布,把能量集中于某一键使其断裂几率是很低的,所以采用预辐照接枝法所需的吸收剂量很大,相关的研究报道很少。
2.
A study was carried out on the preparation of cation-exchange membranes using a one-step method obtained by pre-irradiation grafting of acrylic acid (AA) and sodium styrene sulfonate (SSS) onto high-density polyethylene (HDPE).
高密度聚乙烯预辐照接枝丙烯酸和对苯乙烯磺酸钠单体混合溶液,运用一步法制备了一种羧酸基团和磺酸基团共存的阳离子交换膜,并考察了单体总浓度、辐照剂量、反应温度及交联剂用量诸因素对接枝率的影响规律,找到了实验条件与接枝率的对应关系。
补充资料：氯乙烯和乙烯僧酸乙烯共聚物接枝共聚物
分子式：
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。