1) magnetism optimization
![点击朗读](/dictall/images/read.gif)
磁性优化
1.
The correlation between the stress relief and magnetism optimization of amorphous Fe79B16Si5 alloy during annealing process has been analyzed.
分析了退火过程中应力的松驰与作晶态合金磁性优化之间的联系淬态Fe_(79)B_(16)Si_5非晶合金经退火后,饱和磁感应强度B、提高了72%,最大磁导率μ_m提高22倍,矫顽力H_c和功率损耗P(0。
2) magnetic properties optimization
![点击朗读](/dictall/images/read.gif)
磁性能优化
3) magnetic field optimization
![点击朗读](/dictall/images/read.gif)
磁场优化
1.
A magnetic field optimization model for an aluminum reduction cell was built,which was based on calculating the magnetic field by using the spline integral equation method and considering all factors affecting the current efficiency.
在样条积分方程法计算铝电解槽磁场的基础上,针对影响铝电解槽电流效率的各种因素,建立了铝电解槽的磁场优化模型。
5) optimization of excitation
![点击朗读](/dictall/images/read.gif)
励磁优化
6) electromagnetic optimize
![点击朗读](/dictall/images/read.gif)
电磁优化
补充资料:磁性材料2.薄膜磁性材料
磁性材料2.薄膜磁性材料
Magnetie Materials 2.Thin Film
在一定外加磁场作用下,其反磁化畴(磁矩取向与外磁场方向相反的畴)变为圆柱形磁畴。从膜面上看,这些柱形畴好像浮着的一群圆泡,故称磁泡或叫泡踌(另见磁性材料2.昨晶态磁性材料)。在特定的电路图形、电流方向和一定磁场情况下,可做到控制材料中磁泡的产生、传翰和消失,实现信息的储存和逻辑运算的功能。磁泡的直径在微米量级(0 .5~5协m),每个磁泡的迁移率在1 .26~12.6em八s·A/m)〔 102一i03cm八s·oe)〕,因而可制成存储密度为兆位/cmZ(Mbit/cmZ)和数据处理速率为兆位/s(M肠t/s)的运算器件。磁泡器件经过近20年研究和开发,已取得广泛的实际应用。 对磁泡材料的主要要求是:(l)各向异性常数凡>粤斌,磁化强度从>外磁场强度H;(2)杂质缺陷小,2一~”~’.J泌~-一‘产’~~一~一’、~尹一~~~’J”均匀性好。目前研究得比较清楚的有铁氧体单晶薄膜和稀土一过渡金属薄膜。从制备工艺和性能稳定、器件开发等情况看,以铁氧体磁泡材料比较成熟,早期是用钙钦石型铁氧体单晶片来作磁泡材料,后为YIG单晶薄膜所取代。它是用液相外延法在Gd3Ga5OI:(简称GGO)基片上生成的单晶薄膜,其厚为微米量级。表4为稀土石榴石R3FesolZ的磁性;表5为一些磁泡材料的基本特性数值。农4稀土石抽石R.Fe‘ol,的磁性┌───────────┬────┬────┬────┬────┬────┬────┬────┬────┬─────┬────┬────┐│R │Y │Sm │EU │Gd │Tb │Dy │、Ho │Er │T】11 │Yb │Lu │├───────────┼────┼────┼────┼────┼────┼────┼────┼────┼─────┼────┼────┤│补偿温度,~p,K │ 560 │ 560 │ 570 │ 290 │ 246 │ 220 │ 136 │ 84│4