1) low molecular weight unsaturated polyester
低分子量不饱和聚酯
1.
The morphology of zinc -neutralized sulfonated EPDM (Zn-SEPDM) plasticized with low molecular weight unsaturated polyester (GR) was studied through DSC,XPS, SAXS.
用差示扫描量热法（DSC）、X光电子能谱（XPS）、小角X射线散射（SAXS）、动态力学分析（DMA）和透射电子显微镜（TEM）对低分子量不饱和聚酯（GR）增塑的EPDM磺酸锌盐（Zn-SEPDM）的形态结构进行了研究。
2) high molecular polyether polyol
高分子量低不饱和度聚醚
3) unsaturated polyester putty
不饱和聚酯腻子
1.
Design principle of formulation, manufacture process, performance test, train-spraying test and application investigation of unsaturated polyester putty used on train are introduced.
介绍了铁路客车用不饱和聚酯腻子配方设计原理、生产工艺、性能试验、涂车试验及运用调查等。
5) low shrink unsaturated polyester resin
低收缩不饱和聚酯树脂
6) unsaturated polyester
不饱和聚酯
1.
Study on preparation and characterization of flame retardant unsaturated polyester/montmorillonite nanocomposite;
不饱和聚酯/蒙脱土阻燃纳米复合材料的制备及表征
2.
Tolulene diisocyanate modified unsaturated polyester with high elongation;
具有高伸长率的二异氰酸酯改性不饱和聚酯
3.
Studies on tunable F-P cavity based on doped unsaturated polyester;
基于掺杂型不饱和聚酯的可调谐F-P腔的研究
补充资料：低收缩不饱和聚酯树脂
分子式：
CAS号：
性质：含低收缩添加剂(主要是热塑性树脂)的不饱和聚酯树脂。树脂的体积收缩率可由7％～10％缩小至0.2％。常用的低收缩添加剂按其在苯乙烯中的溶解度分为可溶性添加剂，如聚苯乙烯；不溶性添加剂，如聚乙烯、聚丙烯和乳液法生产的聚氯乙烯；溶胀性添加剂，如氯乙烯-醋酸乙烯共聚物其中聚乙烯、聚丙烯和树脂的相容性差，模压流动性欠佳。由低收缩树脂制得的制品，表面光洁、波纹度小，强度好，收缩率低。主要用于制造片状模塑料和团状模塑料，适于模塑精度要求高的结构部件，供电器、汽车、仪表等部门应用。
CAS号：
性质：含低收缩添加剂(主要是热塑性树脂)的不饱和聚酯树脂。树脂的体积收缩率可由7％～10％缩小至0.2％。常用的低收缩添加剂按其在苯乙烯中的溶解度分为可溶性添加剂，如聚苯乙烯；不溶性添加剂，如聚乙烯、聚丙烯和乳液法生产的聚氯乙烯；溶胀性添加剂，如氯乙烯-醋酸乙烯共聚物其中聚乙烯、聚丙烯和树脂的相容性差，模压流动性欠佳。由低收缩树脂制得的制品，表面光洁、波纹度小，强度好，收缩率低。主要用于制造片状模塑料和团状模塑料，适于模塑精度要求高的结构部件，供电器、汽车、仪表等部门应用。