1) the breakout of longitudinal cracks in corner
角部纵裂漏钢
2) longitudinal-crack steel leak
纵裂漏钢
1.
The reason for longitudinal-crack steel leak is analyzed, some measures formed, better result got.
对板坯连铸机产生的纵裂漏钢原因进行了分析,通过制订改进措施,取得了较好的效果。
3) steel breakout caused by broken corner
角裂漏钢
1.
The effect of steel composition, operating parameters and equipments on deformation of continuous-casting billet and steel breakout caused by broken corner based on site investigation, measuring and statistics to caster production in No.
通过对唐钢第一炼钢厂仿罗可普连铸机生产的连铸小方坯的现场调查、测试和统计,分析了连铸小方坯变形和角裂漏钢的特点及规律,系统研究了钢液成分S含量和[Mn]/[S]、C含量、P含量,连铸工艺参数浇注温度、结晶器冷却、二次冷却水量、冷却均匀性和设备状况结晶器倒锥度、结晶器振动偏摆、引锭杆不对中等因素对连铸小方坯的变形和角裂漏钢的影响。
4) longitudinal corner crack
角部纵裂
1.
Due to frequent emergencies of bleeding out by the billet longitudinal corner crack,the characteristic and mechanism of bleeding out are analyzed.
由于方坯角部纵裂漏钢事故频繁,通过分析漏钢的特点和机理,认为造成小方坯角部纵裂漏钢的主要原因是结晶器倒锥度小、结晶器液面波动及中间包过热度大、结晶器冷却水质差。
2.
1 steelmaking plant of WISCO in 2006 have been made and the main characteristics and mechanism of sticking breakout and longitudinal corner crack induced breakout analyzed.
统计了武钢一炼钢厂方坯连铸机2006年的漏钢情况,分析了粘结漏钢和角部纵裂漏钢的特点及机理,并找出了产生粘结漏钢和角部纵裂漏钢的主要原因是保护渣的性能、结晶器的精度、钢水的过热度、拉速及浸入式水口的对中等。
5) cracking breakout
裂纹漏钢
1.
The most reason of cracking breakout is badness of arc and high temperature of molten steel and high withdrawal speed.
通过统计分析板坯连铸生产中出现的漏钢事故,认为钢水温度低、拉速快和保护渣理化性能不合理易导致粘结漏钢;对弧不良、钢水温度高、拉速快是造成裂纹漏钢的主要原因;开浇和接头漏钢主要是中间包上水口和塞棒烘烤效果不好及出苗时间不足造成的。
2.
By analyzing the statistical data of the past two years,the results indicate that the primary types of breakout are the sticking and cracking breakout in No.
通过对近两年来的数据统计,分析发现邯钢三炼钢厂1号板坯连铸机漏钢类型主要属粘结漏钢和裂纹漏钢两种形式。
6) longitudinal crack at deflec-tion angle
偏离角纵裂
补充资料：纵裂
longitudinalcrack：平行于炭化室内热流方向的焦炭裂纹。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。