2) cobalt-boron alloy
钴硼合金
1.
Magnetic cobalt-boron alloy deposits were prepared by electroless plating.
钴硼合金在镀态下为非晶态结构 ,经热处理后 ,镀层向晶态转变 ,在 40 0℃时 ,硬度和矫顽力达最大。
3) Co-B alloy
钴硼合金
1.
The preparation process for electroless deposition of Co-B alloy nanocrystalline coating is investigated by using perpendicular method and its deposition rate is also studied, thus obtaining optimum process parameters.
采用正交实验法探索了化学沉积钴硼合金纳米晶涂层的制备工艺 ,并对其沉积速率进行了研究 ,从而得出较优的工艺参数 ,同时详细讨论了硫酸钴、酒石酸钠、DMAB(二甲基胺硼烷 )、温度等因素对沉积速率的影响。
4) Ni-B alloy
镍硼合金
1.
The possibility of the electroplating process applied to Ni-B alloy was studied.
研究了用电镀法制取镍硼合金的可能性。
5) Ni B alloy
镍硼合金
1.
The research of complex Ni B alloys and composite electroless Ni B depositions are also briefly introduced.
综述了化学镀镍硼合金的发展状况、化学镀二元镍硼合金的制备工艺、组织结构和性能以及热处理工艺的研究现状 ,并简要介绍了多元及复合化学镀镍硼合金的研究进展 ,展望了该领域的发展应用前
6) chromium-boron alloy
铬硼合金
补充资料：钯硼合金
分子式：
CAS号：
性质：是钯基添加硼的二元合金。硼含量在0.7%～0.8%时，选择性透氢性能最好，有PdB0.23，PdB0.7和PdB0.76等合金牌号。它们的透氢速度36.6～38.7cm3/cm2·min,纯钯为17.8cm3/cm2·min。PdB1.8的阻力数（250℃）8.53×10-2Ω·㎜2/m。硼含量超过1%，加工困难；超过2%，合金性脆不能加工。用作高纯氢净化材料和高温钎料。
CAS号：
性质：是钯基添加硼的二元合金。硼含量在0.7%～0.8%时，选择性透氢性能最好，有PdB0.23，PdB0.7和PdB0.76等合金牌号。它们的透氢速度36.6～38.7cm3/cm2·min,纯钯为17.8cm3/cm2·min。PdB1.8的阻力数（250℃）8.53×10-2Ω·㎜2/m。硼含量超过1%，加工困难；超过2%，合金性脆不能加工。用作高纯氢净化材料和高温钎料。