1) silicoboronitriding
硅硼氮共渗
2) boronitriding
硼氮共渗
1.
Study on improving the hot forging dies service life of 5CrMnMo Steel of boronitriding;
硼氮共渗提高5CrMnMo钢热锻模使用寿命的研究
2.
Research for the Structures, Properties and the Mechanism of Borosulphurizing and Boronitriding;
硼硫、硼氮共渗组织和性能及其机理的研究
3.
Microstructure of the boronitriding layer on austenitic stainless steel and the transition zone between the layer and matrix has been examined.
研究了奥氏体不锈钢硼氮共渗渗层及过渡区组织结构,并对共渗机理进行了探讨。
3) N-B co-penetration
氮硼共渗
1.
Study on binary N-B co-penetration character of No.45 steel in lower temperature condition;
针对目前渗硼存在温度高、脆性大等一系列问题,对45钢进行气体低温氮硼共渗得到复合渗层,并对渗层进行金相组织观察、显微硬度测试,探讨了渗层的形成过程及渗剂中催渗剂尿素的作用。
4) boronsiliconizing
硼硅共渗
1.
The influences of aluminosiliconizing and boronsiliconizing on the microstructure and oxidation resistance of the coatings were researched.
用粉末固体渗法在钼合金表面制备了MoSi2渗层,研究了铝硅共渗和硼硅共渗对渗层的结构和抗氧化性能的影响。
5) Re-B-C-N multi-element penetration
稀土硼碳氮共渗
1.
RE-B-C-N multi-element penetration of 65Mn steel metal rubber with larger wire diameter
大丝径65Mn金属橡胶稀土硼碳氮共渗
6) boronitriding adding RE
加稀土硼氮共渗
补充资料：碳氮硼三元共渗
分子式：
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
CAS号：
性质：碳氮硼三元共渗是使钢制工件同时渗入碳、氮、硼三种元素的化学热处理工艺。共渗后渗层的硬度较渗硼为低(HV600～1000)。碳氮硼三元共渗如用于石油机械易损零件，能提高使用寿命。碳氮硼三元共渗后空冷即可得到HV750的硬度，对于上述钢材制造的薄小工件，可以省去淬火工序。碳氮硼三元共渗也可以在气体介质中进行，例如用尿素(2500g)、甲醇(8L)、硼酸三甲酯(5L)、丙酮(6L)的混合渗剂滴入840~860℃的井式渗碳炉中，保温3～5h后，在低碳合金渗碳钢上可得到0.4～0.6mm渗层，表面硬度达HRC63～65，甚至更高。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。