2) physical phase changes after exposure high temperature
高温后物相变化
3) Phase variation process of oxides
氧化物的相变过程
4) phase transformation
物相转变
1.
The influence of F~- on the phase transformation of alumina from metastable phase toα- alumina and microstructure ofα-alumina has been studied by TG/DSC,XRD,SEM measurements in this paper.
运用TG/DSC、XRD、SEM等分析技术,研究了F~-对氧化铝物相转变及α-氧化铝显微结构的影响。
2.
The phase transformation of carbon alpha-Al(OH)_3 powder in the calcine process between 200 ℃～1 500 ℃ was analyzed using D/Max-3BX beam diffraction meter.
采用D/max-3B X射线衍射仪分析了碳分-αAl(OH)3粉体在200℃~1 500℃煅烧过程中的物相转变,研究了煅烧产物的比表面积、安息角、松装密度、有效密度、折光率、白度、灼减等物理化学性质的变化,该成果已在化学品氧化铝生产中得到应用。
3.
It was discovered that MgO could restrain the phase transformation of metastable alumina to stable α-Al2O3 and change the crystallization habit of α-Al2O3.
研究发现,MgO可以抑制亚稳态氧化铝向稳定态α-Al2O3的物相转变,同时还可以改变α-Al2O3的结晶习性,在没有添加剂的作用下,生成的α-Al2O3是蠕虫状空间网状结晶,在MgO作用下,α-Al2O3晶粒细小,晶粒之间的结合不规则,其原因在于MgO是一种高挥发物质,与Al2O3反应,与在α-Al2O3的晶界处形成MgAl2O4,阻止α-Al2O3晶粒生长。
5) mineral phase transformation
矿物相变
1.
According to the damage features of the fracture types and their developing patterns,and changing of mineral phase transformation under microscopic scale,it is concluded that the superposition between fracturing and explosive spalling plays a key role in the multi-layer damages of the lining concrete.
在显微尺度下受损混凝土裂隙的类型及其扩展规律和矿物相变显示了,中等损伤程度下裂隙的扩展和爆裂作用的叠加是衬砌混凝土发生多层剥落的重要原因;受火混凝土颜色的变化主要与矿物相变和微裂隙的形成有关。
6) phase transition
物相转变
1.
The features of the phase transition for α-Al(OH) 3 powder silts in the calcination process from 200 ℃ to 1 500 ℃ have been studied by D/max-3BX-ray diffractometer,and the physical and chemical properties involved with spectfic surface area,angle of repose,apparent density,effective density,refractive index,whiteness and ignition loss and so on for calcinated product have been studied too.
采用D max - 3BX射线衍射仪分析了α-Al(OH) 3 粉体在 2 0 0～ 15 0 0℃煅烧过程中的物相转变特征 ,研究了煅烧产物的比表面积、安息角、松装密度、有效密度、折光率、白度、灼减等物理化学性质的变
2.
The features of the phase transition for α-Al(OH) 3 powder silts in the calcination process from 200℃ to 1500℃ have been studied by D/max-3BX-ray diffractometer,and the physical and chemical properties involved with spectfic surface area,angle of repose,apparent density,effective density,refractive index,whiteness and ignition loss and so on for calcinated product have been studied too.
本文采用D/max -3BX射线衍射仪分析了α -Al(OH) 3粉体在 2 0 0～ 1 50 0℃煅烧过程中的物相转变特征 ,研究了煅烧产物的比表面积、安息角、松装密度、有效密度、折光率、白度、灼减等物理化学性质的变化。
补充资料：气候要素日变化和年变化
气候要素日变化和年变化
diurnal variation and annual variation of climatic elements
q ihou yaosu ribianhua hen一anb一anhua气候要素日变化和年变化(diurnal varia-tion and annual variation of elimatieelements)由地球自转和公转所引起的以l」、年为周期的气候要素变化。 日变化以气温为例，其日变化与地面加热状况直接有关，最高值在14一15时出现，最低值在日出前后测点的纬度、海拔高度、下垫面条件、季节以及人气干湿状况都可影响气温日变化，但不改变其主要性质)干旱地区夏季的气温日变化最显著，日较差(最高温度与最低温度之差)最大。气温日较差人小对农作物生长有收要意义，是农业气候分析的项目之一水汽压的日变化决定于地面加热条件、地面湿润状沉和湍流交换强弱。在充分湿润的地区和季节.水汽压最高值是午后最大，玄青晨最小，在其它地区，水汽压日变化曲线人多旱双峰型，两个高值分别出现在9时和「1落前后，两个低值发生在日出前和午后〔如图所示、风速日变化上要取决于近地层中湍流交换的日变化，11间因湍流加强，地面风速也增大，午后风速达最大值，夜间风速最小。沿海的海陆风现象及山区山谷风现象也属风的日变化，它们的速度和方向均有周日变化。 年变化气候要素年变化与太阳辐射年变化有关最明显的是气温年变化，在北回归线以北的北半球大陆上，l月气温最低，7月最高，气温年变曲线比之天文辐射年变曲线约有一个月的位相落后。在海洋l比日︸1 一一 。dq\汉俐田仁书5言 1 2 16时间/h20 24水气压的日变化上气温年变曲线的位相落后更多。从各地气温年变化特点就可看出海陆影响的程度(见大陆度)。降水的年变化也很明显，中国东部地区因受季风影响，夏季6一8月降水最多，冬季最少，干湿季竹交替明显地中海沿岸降水年变化具有冬季降水充沛，夏季少雨的特点，形成特殊的地中海气候。在英lfil各地，全年各月降水墩分配相当均匀，年变化较小，反映出典型的海洋性气候相对湿度的年变化与气温年变化相反，一般是夏季小冬季人。气温、降水、相对湿度等要素年变曲线的配置特点，可反映出各地气候的特点 (翁笃鸣)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条