1) (Ti,Me)(C,N)/Ni system
(Ti,Me)(C,N)/Ni体系
3) Ti-C-Ni-Al system
Ti-C-Ni-Al体系
4) Ni-Ti-Si system
Ni-Ti-Si体系
5) Fe-Ti-C system
Fe-Ti-C体系
1.
Effect of preset heating rate on combustion synthesis of Fe-Ti-C system under the action of electric field;
预设升温速度对电场作用下Fe-Ti-C体系燃烧合成的影响
2.
Using Gleeble-1500D thermal simulation equipment, the effect of Fe content on the low temperature combustion synthesis process of Fe-Ti-C system and microstructure features of the products were studied in this study.
采用Gleeble-1500D热模拟机,对电场作用下Fe含量对Fe-Ti-C体系低温燃烧合成过程和产物显微结构特征的影响进行了研究。
3.
Using Gleeble-1500D, the effect of incubation process on the low temperature combustion synthesis process of Fe-Ti-C system under several technological conditions was studied.
采用Gleeble-1500D热模拟机,在电场作用下,研究保温过程对几种工艺条件下Fe-Ti-C体系压坯低温燃烧合成过程的影响。
6) Ti-C-Fe system
Ti-C-Fe体系
补充资料：Ti-Ni based memory alloy
分子式：
CAS号：
性质：具有形状记忆效应的TiNi金属间化合物。与其他金属间化合物不同，它具有很高的塑性。该合金具有较大的形状记忆应变(6％～10％)和较高的恢复应力(200～760MPa)。合金在马氏体状态屈服强度为100～200MPa，奥氏体状态屈服强度约在200～700MPa之间，断裂强度约700～1000MPa。在Af以上加载，卸载后显示超弹性行为，在适宜温度范围内热-机械处理后显示双程形状记忆效应。具有较高记忆寿命，预应变<0.5％，循环次数可在107以上。TiNi记忆合金还包括TiNi-Cu、TiNi-Co、TiNi-Fe和TiNi-Nb等具有较高实用价值记忆合金，其中Ti50Ni47Fe3合金是制造管接头等紧固件的良好材料。
CAS号：
性质：具有形状记忆效应的TiNi金属间化合物。与其他金属间化合物不同，它具有很高的塑性。该合金具有较大的形状记忆应变(6％～10％)和较高的恢复应力(200～760MPa)。合金在马氏体状态屈服强度为100～200MPa，奥氏体状态屈服强度约在200～700MPa之间，断裂强度约700～1000MPa。在Af以上加载，卸载后显示超弹性行为，在适宜温度范围内热-机械处理后显示双程形状记忆效应。具有较高记忆寿命，预应变<0.5％，循环次数可在107以上。TiNi记忆合金还包括TiNi-Cu、TiNi-Co、TiNi-Fe和TiNi-Nb等具有较高实用价值记忆合金，其中Ti50Ni47Fe3合金是制造管接头等紧固件的良好材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。