1) V_2O_5/TiO_2
V_2O_5/TiO_2
1.
Using porous metatitanic acid,which was prepared by hydrolysis of industrial titanyl sulfate (TiOSO_4)solution under boiling condition,as a carder,the aqueous solution consists of hydrogen peroxide and ammonium metavanadate as a pickling agent,the V_2O_5/TiO_2 catalysts with different V_2O_5 content were obtained after the steps of impregnation, dehydration and calcination.
以工业 TiOSO_4液为钛源,在沸腾条件下水解制得多孔偏钛酸作为载体,以双氧水溶解偏钒酸铵(NH_4VO_3)为浸渍液,浸渍、干燥、煅烧得到不同钒负载量的 V_2O_5/TiO_2催化剂。
2) V_2O_5/TiO_2
V_2O_5/Ti_O_2
3) V_2O_5-TiO_2
V2O5-TiO2
1.
Transparent V_2O_5-TiO_2 composite nanometer thin films on glass substrates were prepared with sol-gel method and dip-coating technique to study the effect of titanium oxide addition on water contact angle,crystal phase and size.
为了研究钒的掺杂对TiO2薄膜的接触角、晶型及晶粒粒径的关系,采用sol-gel制备了V2O5-TiO2复合薄膜和复合粉末并对其进行表征分析。
4) V_2O_5/TiO_2 Catalysts
V_2O_5/TiO_2催化剂
1.
Studies on V_2O_5/TiO_2 Catalysts for Ammoxidation of 3-Picoline;
3-甲基吡啶氨氧化V_2O_5/TiO_2催化剂研究
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。