1) polar grafted polymer
极性接枝物
1.
A polar grafted polymer which has an affinity for carbon surface was introduced in the heating system, which in turn stabilize CB particals.
提出了一种改善有机ＰＴＣ导电材料电性能重复稳定性的新途径，即在发热体材料中导入一种与碳黑粒子表面有亲和性的极性接枝物作为第三组分，使其在界面形成一种所谓“束缚组成物”或“相互贯入型树脂组成物”，使碳黑粒子在基体中分散稳定。
2) partial blocking polar polymer
部分封端极性接枝共聚物
3) grafting copolymer of amphoteric guar gum
两性接枝共聚物
4) elastomer grafts
弹性体接枝物
1.
The flame retardant polyamide 6 (PA6)/Mg(OH)_ 2 composites was prepared by blending Mg(OH)_ 2,elastomer grafts, antioxidant and PA6.
将Mg(OH)2、弹性体接枝物、抗氧剂与尼龙6(PA6)共混制得阻燃PA6/Mg(OH)2复合材料,探讨了两种弹性体接枝物对PA6/Mg(OH)2复合材料力学性能和阻燃性能的影响。
6) graft copolymer
接枝物
1.
Graft copolymers(SPI-g-NH-PAMPS)were prepared by a graft reaction between the free carboxylic acid groups of soy protein isolate(SPI)and the amino groups of poly(2-acrylanmido-2-methyl propane sulfonic acid)(H_2N-PAMPS)using 1-(3-(dimethylamino)propyl)-3-ethyl-carbodiimide hydrochloride/N-hydroxysuccinimide as the condensing agents in a buffer solution.
再用1-(3-二甲氨基丙基)-3-乙基碳二亚胺盐酸盐(EDC)和N-羟基琥珀酰亚胺(NHS)在室温下催化H2N-PAMPS的端氨基与大豆分离蛋白(SPI)的羧基反应形成酰胺键,得到接枝物SPI-g-NH-PAMPS。
补充资料：氯乙烯和乙烯僧酸乙烯共聚物接枝共聚物
分子式：
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。