1) static and metadynamic softening
静态和亚动态软化
2) static softening
静态软化
1.
The static softening behavior of C-Si-Mn dual-phase steel as-hot-rolled using double-stage hot compression was studied on Gleeble 1500 tester.
采用后插法计算了在不同真应变条件下的静态再结晶率,通过双道次压缩测试静态软化动力学的实验表明,实验钢变形后很容易发生静态软化。
2.
The static softening behavior of hot deformation austenite of pipeline steel X60 and low-carbon bainitic steel JB700 were studied on MMS-100 thermal simulator,the effects of deformation temperature,strain magnitude and isothermal time on static softening rate were analyzed.
利用MMS-100热力模拟试验机研究了X60管线钢和JB700低碳贝氏体钢在不同变形温度、变形程度和变形后等温保持时间对奥氏体静态软化行为的影响。
3.
The dynamic and static softening behaviors of 2519 aluminum alloy in multi-stage hot compression were studied.
在Gleeble 1500热力模拟机上,采用双道次间隙式等温热压缩试验,对2519铝合金多道次热压缩变形过程中动态与静态软化特性进行了研究,变形温度为300 ~ 500 ℃,应变速率为0。
4) dynamic softening
动态软化
1.
The results show that the considerable dynamic softening and ex.
研究结果表明:在500 ℃时,2519铝合金流动应力由于结构软化而存在相当强的动态软化和奇异的静态软化,导致第2道次的起始流动应力比前一道次的起始流动应力低;在热压缩变形道次间保温停歇后,流变应力出现明显的软化现象,保温停歇时间越长,合金软化率越高;变形及停歇保持温度越高,合金软化越严重。
2.
The compress during single and double passes for boron microalloyed steel was simulated using a gleeble-1500 thermal simulation testing apparatus, The quantitative effect of deformation temperature(T)、deformation degree(ε)、deformation rate(ε·)、primary grain size(d_0)、and interval time between passes(t)on static state and dynamic softening fraction(X)was obtained by nonlinear regression analysis.
运用gleeble-1500热模拟试验机November对含硼微合金钢进行了单、双道次压缩模拟,并通过非线性回归分析得到了静态与动态软化百分比(X)与变形温度(T)、变形程度(ε)、变形速率(ε·)、原始晶粒尺寸(d0)、道次间隔时间(t)之间的关系。
3.
It was indicated that the considerable dynamic softening and exceptional softening associate with a struc.
结果表明:在400℃时,1050和7075铝合金流动应力由于结构软化而存在相当强的动态软化和奇异的静态软化,导致第二道次的起始流动应力比前一道次的起始流动应力低;对于所有合金,静态软化随着变形温度和道次间保温及停留时间的增加而增加;但是在同一变形条件下,5182铝合金的静态软化速率比1050和7075铝合金高。