1) Si/C/N nanocomposite powder
Si/C/N纳米复合粉
2) nano Si/C/N composite powder
纳米Si/C/N复相粉体
1.
The nano Si/C/N composite powders was synthesized from hexamethyldisilazane ((Me3Si)2NH) (Me:CH3) by a laser-induced gas-phase reaction.
用激光诱导气相反应法,以六甲基二硅胺烷(Me3Si)2NH)(Me:CH3)为原料,用双反应室激光气相合成纳米粉体装置合成了纳米Si/C/N复相粉体,复相粉体的粒径为20-30 nm,纳米粉体的分散性好,无严重团聚。
3) nano Si/C/N
Si/C/N纳米粉
4) Si/C/N nanopowders
Si-C-N纳米粉体
1.
For improving dispersion properties of Si/C/N nanopowders,the dispersion behavior of Si/C/N nanpowders exposured in air for long time in water was investigated by methods of adding surfactant,mechanical stirring and adjusting pH values of the water.
采用添加表面活性剂、机械搅拌、调节pH值等手段,对长期暴露于空气中的Si-C-N纳米粉体在水介质中的分散行为进行了研究。
5) Si/C/N nanpowders
Si/C/N纳米粉体
1.
For improving dispersion of the nano suspensions,the dispersion behavior of Si/C/N nanpowders in water-ethyl carbamate organic liquids by high muddy force is investigated.
Si/C/N纳米粉体具有活性高、难以在水中进行分散的特点。
6) Si-C-N nano-powders
Si-C-N纳米微粉
1.
The in-site toughening Si3N4 ceramic,synthesis of Si-C-N nano-powders and nano-powders reinforced Si3N4 were the main content in this thesis.
本文以自增韧Si_3N_4陶瓷、Si-C-N纳米微粉的合成以及纳米微粉增强Si_3N_4陶瓷为研究对象，研究了烧结助剂对自韧Si_3N_4陶瓷力学性能与显微结构的影响；揭示了不同原料配比与氨解先驱体的性能和结构的关系，研究了先驱体在不同气氛下裂解对纳米微粉的组成、结构的影响；对纳米微粉增强Si_3N_4陶瓷的组成、结构、性能与增强增韧机制以及氧化与热震行为进行了较系统的研究与分析。