1) α-high strength mould plaster
α-高强模型石膏
1.
This paper describes the property of α-high strength mould plaster and its application in native and foreign countries,and introduces the technical requirements for plaster mould design and fabrication,and the process of plaster mould fabrication.
介绍了α-高强模型石膏的特点及国内外应用简况;对该石膏模具的设计与制造提出了技术要求,并介绍了制造工艺过程;对其应用效果作了分析;针对目前国内应用中存在的主要问题,提出了解决措施。
2) α-type high-strength gypsum
α型高强石膏
3) high strength α-hemi-hydrated gypsum
高强α-半水石膏
1.
Research on crystal form modifying agent and technological parameters of high strength α-hemi-hydrated gypsum made with desulfogypsum;
脱硫石膏制备高强α-半水石膏的晶形改良剂与工艺参数研究
5) modle gypsum
模型石膏
1.
The present paper delt with the influence of several additives such as water reducing agent of N and colloidal silica on the performances including setting time and strength and absorption rate and attack rate of modle gypsum,.
研究了N型减水剂、硅溶胶等添加剂对模型石膏凝结时间、强度、吸水率、溶蚀率等性能的影响,并确定了有关性能与添加量之间的关系,得出了最佳添加量。
6) plaster cast
石膏模型
1.
After correction,all the patterns were evaluated,so the best pattern was chosen and compared with the plaster cast and the relationship could be found.
为更加准确地定量分析旗袍空间省量分配和侧缝线的形态关系,以旗袍基本纸样为基础变化出5种不同的省量分配方案的纸样,制作成样衣并修正;对5种纸样进行了综合评价,将具有最好效果的纸样和石膏模型展开图覆合,分析了省量分配与侧缝形态的关系。
补充资料：模型石膏
分子式：
CAS号：
性质：制造模型用的半水石膏。天然石膏（CaSO4·2H2O）经粉碎、炒制，使其脱去1.5个结晶水后得到半水石膏（CaSO4·1/2H2O）。炒制前的石膏一般要过80～120目筛。炒制温度控制在150～200℃为宜。炒制石膏温度不易稳定，所炒制的石膏中除β型半水石膏外，还含有少量二水石膏及无水石膏（又称死烧石膏），后两者不易水化。需经1～2d陈化，使他们向半水石膏转化，同时也可避免新炒制的石膏水化过剧，影响石膏模质量。
CAS号：
性质：制造模型用的半水石膏。天然石膏（CaSO4·2H2O）经粉碎、炒制，使其脱去1.5个结晶水后得到半水石膏（CaSO4·1/2H2O）。炒制前的石膏一般要过80～120目筛。炒制温度控制在150～200℃为宜。炒制石膏温度不易稳定，所炒制的石膏中除β型半水石膏外，还含有少量二水石膏及无水石膏（又称死烧石膏），后两者不易水化。需经1～2d陈化，使他们向半水石膏转化，同时也可避免新炒制的石膏水化过剧，影响石膏模质量。