1) specific compression strength
比压强度
1.
It found that the compression strain and the permanent compression set values were required to be 20%~25% and under 5% respectively,the specific compression strength was 3.
结果表明,当弹性体的压缩应变在20%/～25%,压缩永久变形率在5%以下时,TPVC比压强度为3。
2) specific compress strength
比压缩强度
1.
The results showed that adding glass microspheres could effectively reduce the density of materials and increase the specific compress strength,when the volume fraction ofhollow glass microspheres was about 55 percent,the materials reached thehighest specific .
结果表明,玻璃微珠的加入,能有效降低材料的密度,提高材料的比压缩强度,当空心玻璃微珠体积分数在55%左右时,材料的比压缩强度最大,玻璃微珠表面与树脂基体间界面粘结状况最好,此时玻璃微珠在树脂基体中均匀分散。
3) compressive strength ratio
抗压强度比
1.
Research and application of detection method to compressive strength ratio for pump antifreezer;
混凝土泵送防冻剂抗压强度比检测方法的研究与应用
4) ratio of rock's compressive tensile strength
压拉强度比
5) Ratio of tensile strength to compressive strength
拉压强度比
6) the method of specific strength
比强度法
1.
Using the method of specific strength,the pozzolanic effect of fly-ash in recycled aggregate concrete has been researched,comparing with natural aggregate concrete in the same mixing ratio,the pozzolanic effect of fly-ash in recycled aggregate concrete is weaker than in the other concrete.
本文采用比强度法分析研究了粉煤灰在再生混凝土中的火山灰效应,并与同配比对比混凝土相比较,得出了粉煤灰在再生混凝土中的火山灰活性较在对比混凝土中小的结论。
补充资料：等离子体压强和磁压强
在流体近似下，可以把等离子体看成是彼此相互作用的电子和离子两种气体的混合物。它们各具有动力压强,上述两种气体成分的分压强之和P=k(niTi+neTe)称为等离子体压强，k是玻耳兹曼常数,角标i、e分别表示离子和电子。
经常遇到的处在静磁场 B中的等离子体，除了等离子体压强外，它还受到磁力 作用，j是电流密度。当磁力线是直的并互相平行时，(B·墷)B项等于零，相当于压强，称为等离子体磁压强。
在等离子体压强和磁压强并存之时，常用参数表示磁压强的相对重要性。这个参数称为比压。
经常遇到的处在静磁场 B中的等离子体，除了等离子体压强外，它还受到磁力 作用，j是电流密度。当磁力线是直的并互相平行时，(B·墷)B项等于零，相当于压强，称为等离子体磁压强。
在等离子体压强和磁压强并存之时，常用参数表示磁压强的相对重要性。这个参数称为比压。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条