1) X-13 molecular sieve
X-13分子筛
2) The SSZ-13 molecular sieve
分子筛SSZ-13
1.
The SSZ-13 molecular sieve can be synthesized by adopting traditional hydrothermal method in the treatise, and the best synthesis ratio and reacting condition were determined through experiments.
本文以硅溶胶、硫酸铝、氢氧化钠、去离子水为原料,以N,N,N-三甲基金钢烷氢氧化铵为模板剂(R),采用传统的水热法合成分子筛SSZ-13,并通过实验确定它的最佳合成配比和反应条件:反应温度为155℃,晶化时间为3天,其最佳氧化物的摩尔比范围为SiO2/A12O3=40,Na2O/A12O3=12-16,R2O/A12O3=3-5,H2O/A12O3=900-1350。
3) ITQ-13 zeolite
ITQ-13分子筛
1.
ITQ-13 zeolite was successfully synthesized using three silica sources,i.
通过三种硅源,正硅酸已脂(TEOS)、胶体二氧化硅、气相法白炭黑,成功地合成出ITQ-13分子筛,并用X射线衍射(XRD)、扫描电子显微镜(SEM)、BET表面积测试和氘代乙腈吸附等方法对合成的材料进行表征。
5) X zeolites
X型分子筛
1.
The research has synthesized X zeolites utilizing industry waste residue-circulation fluidization bed(CFB)fly ash successfully.
利用工业废渣流化床粉煤灰成功合成了X型分子筛,通过XRD衍射表征发现Na2O/SiO2是影响合成分子筛结晶度的关键因素。
2.
X zeolites were synthesized by using industrial waste residue fluent-bed fly ash successfully.
利用工业废渣流化床粉煤灰成功合成出X型分子筛。
6) zeolite X
X型分子筛
1.
A method has been developed by which zeolite X can be grown on the surface of microporous ceramic cylinder on the basis of classical synthesis of zeolite X.
研究X型分子筛在多孔陶瓷载体上的生长条件 ,合成膜的晶化液组成n(SiO2 ) /n(Al2 O3) =3 。
补充资料：13X分子筛
分子式：Na2O·Al2O3·(2～3)SiO·6.0H2O
CAS号：
性质：白色粉末。在吸附质浓度很低时仍具有高吸附能力。由水玻璃、偏铝酸钠、氢氧化钠及定向剂按一定摩尔比混合后发生反应，生成凝胶，经恒温静态结晶，过滤，洗涤，烘干制得13X分子筛原粉，再与粘接剂捏合成型，灼烧活化制得。用于气体干燥和净化，以及脱除汽油中硫分。
CAS号：
性质：白色粉末。在吸附质浓度很低时仍具有高吸附能力。由水玻璃、偏铝酸钠、氢氧化钠及定向剂按一定摩尔比混合后发生反应，生成凝胶，经恒温静态结晶，过滤，洗涤，烘干制得13X分子筛原粉，再与粘接剂捏合成型，灼烧活化制得。用于气体干燥和净化，以及脱除汽油中硫分。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条