1) Hel-PES
Hel紫外光电子能谱(PES)
2) Photoelectron spectroscopy (PES)
紫外光电子能谱(PES)
3) UPS
紫外光电子能谱
1.
Fabrication, microstructure and UPS spectra of Co: BaTiO_3/Si(100) nano-composite films;
Co:BaTiO_3/Si(100)纳米复合薄膜制备、微结构及其紫外光电子能谱研究
2.
The thin films of fluorescein grown on Ag(110) have been studied by the ultraviolet photoemission spectroscopy(UPS).
利用紫外光电子能谱(UPS)对在Ag(110)表面上荧光素(fluorescein)的生长进行研究。
3.
The Ultraviolet Photoelectron Spectra(UPS) of 10 silatranes are recorded in this paper.
报道了 10种杂氮硅三环类化合物的紫外光电子能谱 (UPS) 。
4) ultraviolet photoelectron spectroscopy(UPS)
紫外光电子能谱
1.
The technique of coupling ultraviolet photoelectron spectroscopy(UPS) with time-of-flight mass spectrometry(TOFMS) is described.
本文报道了将紫外光电子能谱(UPS)和飞行时间质谱(TOFMS)相结合的技术。
5) Ultraviolet photoemission spectroscopy
紫外光电子能谱
1.
The growth of perylene and tetracene on Ag (110) has been studied by the ultraviolet photoemission spectroscopy (UPS) and low-energy electron diffraction (LEED).
利用紫外光电子能谱 (UPS)和低能电子衍射 (LEED)对银 ( 110 )表面上perylene与tetracene的生长进行了研究 。
6) ultraviolet photoelectron spectroscopy
紫外光电子能谱
补充资料：PES
聚醚砜是由4，4’-双磺酰氮二苯醚在无水氯化铁催化下，与二苯醚缩合制得。折射率1．85，玻璃化温度225℃，热变形温度203℃(1．82MPa)。耐热性介于聚砜和聚芳砜之间，长期使用温度180-200 ℃。耐老化性能优异，在180 ℃使用可达20年。耐燃性好．即使燃烧也不发烟。耐蠕变性好，在150 ℃和20MPa压力下的应变只有2．55％。耐化学药品性良好，除氯代烃、酮类、酸类以外耐一般有机溶剂。对一般酸、碱、脂肪烃、油脂、醇类等稳定。耐蒸气和过热水(150-160 ℃)性能好，耐紫外线性能较差，电性能优良，耐燃等级V-O。
相对密度 l .37-1．5l
吸水性(23℃／24h) 0. 43%
拉伸强度 84.3-124.5〔23℃)；
41．2-59．8(180℃)
伸长率 40-80％
弯曲强度 129. 4-171．5MPa
冲击强度(缺口) 78．4～85．3J／m
洛氏硬度 R120-134
相对密度 l .37-1．5l
吸水性(23℃／24h) 0. 43%
拉伸强度 84.3-124.5〔23℃)；
41．2-59．8(180℃)
伸长率 40-80％
弯曲强度 129. 4-171．5MPa
冲击强度(缺口) 78．4～85．3J／m
洛氏硬度 R120-134
说明：补充资料仅用于学习参考，请勿用于其它任何用途。