1) BaTiO3 solid solutions
BaTiO_3基固溶体
2) nano-BaTiO_3 solid solutions
纳米BaTiO_3基固溶体
3) BaTiO3 solid solutions
BaTiO_3固溶体
4) V-based solid solution
V基固溶体
1.
Influence of ball-milling with Cu powder on electrochemicalproperties of V-based solid solution type hydrogen storage alloys;
Cu粉复合球磨处理对V基固溶体型贮氢合金电化学性能的影响
2.
Based on XRD and FESEM-EDS analysis, the alloy is mainly composed of V-based solid solution with BCC structure and TiNi-based secondary phase.
本文采用XRD,FESEM-EDS及电化学阻抗谱(EIS)等方法对V基固溶体Ti0。
3.
The result of XRD analysis shows that the alloy is mainly composed of V-based solid solution phase with body-centered-cubic (bcc) structure and C14 Laves phase with hexagonal structure.
X射线衍射分析表明:该合金由体心立方结构(bcc)的V基固溶体主相和少量六方结构的C14型Laves相组成;FESEM及EDS分析表明:V基固溶体主相形成树枝晶,C14型Laves相呈网格状围绕着树枝晶的晶界,元素在两相中的分布呈现镜像关系。
5) CeO2-based solid solutions
CeO2基固溶体
1.
CeO2-based solid solutions (Ce0.
采用柠檬酸溶胶-凝胶法制备CeO2基固溶体催化剂(Ce0。
6) V based solid solutions
V-基固溶体
补充资料：氧化锆基固溶体
分子式：ZrO2
CAS号：
性质：室温稳定的ZrO2是单斜相，在掺杂二价碱土金属氧化物或三价稀土氧化物后，形成萤石型立方固溶体，又称全稳定ZrO2，是氧离子导体。掺稀土比掺碱土金属者有更高的电导率，如在1000℃时，(ZrO2)0.88(CaO)0.12和(ZrO2)0.91(Y2O3)0.09的电导率分别为10-2和10-1S·cm-1。ZrO2基固溶体的离子迁移数近于1，但受氧分压影响，氧分压至一定下限时会出现电子电导。Y2O3稳定的ZrO2固溶体己成功地用作高温燃料电池和氧传感器的隔膜材料。
CAS号：
性质：室温稳定的ZrO2是单斜相，在掺杂二价碱土金属氧化物或三价稀土氧化物后，形成萤石型立方固溶体，又称全稳定ZrO2，是氧离子导体。掺稀土比掺碱土金属者有更高的电导率，如在1000℃时，(ZrO2)0.88(CaO)0.12和(ZrO2)0.91(Y2O3)0.09的电导率分别为10-2和10-1S·cm-1。ZrO2基固溶体的离子迁移数近于1，但受氧分压影响，氧分压至一定下限时会出现电子电导。Y2O3稳定的ZrO2固溶体己成功地用作高温燃料电池和氧传感器的隔膜材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。