1)  hysteresis of energy loss
滞后能耗
1.
Visco elastic hysteresis of energy loss of UHMWPE modified by glass micro spheres and glass fibers was analyzed theoretically and investigated experimentally.
对用超细玻璃微珠和玻璃纤维两种填料改性后的超高分子量聚乙烯的粘弹性滞后能耗 (tanδ)进行了理论分析与试验研究 ,结果发现 :粘弹性滞后能耗 (tanδ)随着填料比例的增加而降低 ,随着温度的升高而增大 ,随频率的增高、降低而变化不大 ,弹性模量随温度升高而降低 ,随频率的增大而增大 ,此外 ,在相同比例时添加超细玻璃微珠比添加玻璃纤维效果更
2)  heat from hysteresis of energy loss
滞后能耗生热
3)  hysteretic energy
滞回耗能
1.
Analysis on seismic behavior of steel-concrete composite frame structure based on hysteretic energy;
基于滞回耗能的钢-混凝土组合框架抗震性能分析
2.
An improved pushover analysis method based on hysteretic energy dissipation;
一种基于滞回耗能的改进pushover分析方法
3.
Estimation of hysteretic energy of structures based on equivalent SDOF systems;
基于等效单自由度体系的结构滞回耗能估计
4)  hysteric energy
滞回耗能
1.
Seismic energy response analyses of 11 tall hybrid structures with different periods are carried out using 10 ground motions of different types,in order to get the relationship of the hysteric energy story weight factor to ground motions and system characteristics.
本文采用10条不同类型地震波对11个周期不同的高层混合结构进行地震能量分析,以研究结构参数以及地震波参数对结构滞回耗能层间分布系数的影响。
5)  dissipated energy
滞回耗能
1.
The damage states,bearing capacities,ductility,dissipated energy and stiffness degradation of specimens are compared when the specimens are subjected to cyclic loading.
5比例钢筋混凝土桥墩试件,对低周反复荷载作用下试件试验破坏形态、承载力、位移延性、滞回耗能、刚度退化等方面进行了比较分析,可以认为基于位移设计的钢筋混凝土桥墩能够达到预期的延性抗震要求,并且在相对耗能能力(与理想弹塑性模型相比)、刚度退化性能方面与现行规范抗震设计方法设计的桥墩相当。
2.
On the basis of the testing results and the double paramentersdamage model, a modification of dissipated energy factor was made for the modelused in CFST structure, which provided a base for the seismic damage calculation of CFST structures.
本文通过实验的方法,研究了钢管混凝土柱在水平载荷作用下的累积滞回耗能问题,采用等价滞回圈数的概念分析了钢管混凝土的低周疲劳损伤问题,并进一步考虑了地震作用下的损伤情况,在双参数累积损伤模型的基础上,根据实验研究结果,通过修改耗能因子,使其损伤模型适用于钢管混凝土结构,为进一步深入地研究钢管混凝土的地震损伤提供了基础。
6)  hysteretic energy dissipation
滞回耗能
1.
This dissertation focused on the Pushover analysis method on the basic of summarizing concerned internal and overseas theory and method, and an evaluation method of seismic capacity of bridge structures is developed based on the adaptive hysteretic energy dissipation spectra-based push-over analysis method, which was validated by some examples.
本文在总结国内外有关理论和方法的基础上,重点研究了Pushover分析方法,利用基于滞回耗能的模态Pushover分析方法对桥梁结构抗震能力进行评估,并通过算例加以验证。
补充资料:初轧能耗


初轧能耗
energy consumption of blooming mill

ehuzha nenghao初轧能耗(energy eonsumption。f bloomingmill)初轧厂在钢锭轧成钢坯的工艺过程中,生产吨钢所消耗的能量,其中包括然料消耗(折合成标准煤)、电耗、水耗等,是钢坯生产的重要的技术经济指标。 初轧能耗约占钢铁企业总能耗的3%,其中加热能耗又占初轧能耗的75%。初轧厂的节能、降耗是提高企业经济效益的重要技术措施之一,是合理利用资源的重要手段。 初轧节能首先着眼于节约加热能耗,采取的主要措施有: (l)提高钢锭装炉温度,减少冷锭率(见冷装)。要求加强炼钢、脱模、初轧及均热之间的联系和管理,作出钢和空炉预报,采用快脱模、快送锭和钢锭保温车等措施,提高送锭温度。 (2)推广钢锭的液芯加热(见保温均热法)和液芯札制工艺,利用钢锭的凝固潜热自身均热等节能工艺; (3)合理控制炉温和加热制度。将钢锭最高加热炉温由1370一1390C降为1330一1340℃。对不同入炉温度的钢锭采用不同的加热制度等; (4)加强均热炉保温措施,减少热损失。如采用优质保温材料耐火纤维、密闭型烟道,三个炉坑并联的上部单烧嘴均热炉等; (5)提高空气预热温度,保证燃料充分燃烧。采用高效换热式预热器,控制废气含氧量等; (6)采用电子计算机对均热炉实行闭环控制。 此外,加强对初轧电耗的控制,制定合理的压下规程和温度一速度制度,充分利用轧件余热(如钢坯连轧、钢坯水冷锅炉等),也都能使初轧系统的能耗进一步降低。 (胡林)
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条