1) Mn B bainitic steels
Mn-B系贝氏体钢
2) Mn-B bainitic steel
Mn-B贝氏体钢
1.
Based on the service condition of coal-mine anchor bolt in China and the previous research result yielded by the authors of this paper,an air-cooled Mn-B bainitic steel with lower carbon content was designed,and its heat treatment process was investigated,too.
根据我国煤矿锚杆的实际使用情况及本课题组已有的研究结果,设计了一种锚杆用空冷低碳Mn-B贝氏体钢,并对其热处理工艺进行了研究。
4) low carbon Mn-B bainitic steel
低碳Mn-B贝氏体钢
1.
Experiments on the fatigue properties , hot working technology and assembled truck verification of the front axle made of low carbon Mn-B bainitic steel have been performed.
对低碳Mn-B贝氏体钢制前轴进行疲劳性能、热加工工艺和装车考核等试验。
5) baintic steel with Mn-Si alloying
Mn-Si贝氏体钢
6) bainite steel
贝氏体钢
1.
Susceptibility to hydrogen embrittlement and dehydrogenation annealing process of bainite steel used for crossing;
辙叉用贝氏体钢的氢脆特性及去氢退火工艺
2.
The changed of micostrure of 20Mn2SiVB bainite steel at constart temperature;
等温过程中20Mn2SiVB贝氏体钢显微组织的变化
3.
Effects of rare earth on microstructure and mechanical properties of GDL-1 bainite steel;
稀土对GDL-1型贝氏体钢的显微组织及力学性能的影响
补充资料：贝氏体钢
分子式：
CAS号：
性质：使用状态下基体的金相组织为贝氏体的一类钢。其化学组成是低碳和低合金元素，含碳量一般<0.05％，主要合金元素是Mn，Cr，Ni，Mo，B等。贝氏体组织通常通过空冷或控制冷却速度得到。这类钢具有高强度(530～1500MPa)、高韧性、抗拉强度随贝氏体转变温度的降低而提高。工艺性能(可焊性和成型性)较好。广泛用于航空、船舶、锅炉、石油化工高压管道以及压力容器等方面。
CAS号：
性质：使用状态下基体的金相组织为贝氏体的一类钢。其化学组成是低碳和低合金元素，含碳量一般<0.05％，主要合金元素是Mn，Cr，Ni，Mo，B等。贝氏体组织通常通过空冷或控制冷却速度得到。这类钢具有高强度(530～1500MPa)、高韧性、抗拉强度随贝氏体转变温度的降低而提高。工艺性能(可焊性和成型性)较好。广泛用于航空、船舶、锅炉、石油化工高压管道以及压力容器等方面。