1) bisamides bis(crown ether)
酰胺型双冠醚
1.
Three bisamides bis(crown ether) compounds are synthesized by the reaction of o、m、p phenylenedioxydiacetyl dichloride with 4′ aminobenzo 15 crown 5;three bisesters bis(crown ether) compounds are synthesized by the comdensation of o、m、p phenylenedioxydiacetyl dichloride with 6 hydroxyl dibenzo 16 crown 5.
用邻、间、对苯二氧乙酰氯分别与4′-氨基苯并-15-冠-5缩合,制得了3种酰胺型双冠醚(8a,8b,8c);再以上述3种二酰氯与6-羟基二苯并-16-冠-5缩合,得到3种双酯型双冠醚(9a,9b,9c)。
2) Bisamide type azacrown ethers
双酰胺型氮杂冠醚
3) parathesin
[pə'ræθisin]
酰胺型开链冠醚
1.
Synthesis and characterizaton of open chain crown ethers with parathesin as terminal group;
以对氨基苯甲酸乙酯为端基的酰胺型开链冠醚的合成与表征
4) mide-type azacrown ether
酰胺型氮杂冠醚
5) Amide type liquid crystalline crown ether
酰胺型液晶冠醚
6) Bisamides-bis(crown ether)
酰胺型双冠酸
补充资料:双马型聚酰亚胺
分子式:
CAS号:
性质:又称聚顺丁二酰亚胺或双马型聚酰亚胺。由双马来酰亚胺中间体制备的聚合物,是加成型聚酰亚胺中一类重要品种。由顺丁烯二酸酐与二元胺在二甲基甲酰胺或丙酮中反应,然后经脱水和化学酰亚胺化,形成双马来酰亚胺中间体(BMI),再经加成聚合反应形成交联结构的聚双马来酰亚胺。中间体溶于二甲基甲酰胺等强极性溶剂,熔融黏度低,固化过程中无低分子物释放,适宜作耐高温结构胶黏剂、绝缘浸渍漆、模塑料,尤其适用作高性能复合材料基体树脂。均聚物的玻璃化温度大于300℃,可在180~230℃长期使用,因性脆限制了应用。改性的方法很多:(1)合成不同组成或结构的二元胺以及氨基封端的芳醚砜、芳醚酮、有机硅、酰胺-酰亚胺或介晶单元的预聚物,制备相应的双马来酰亚胺中间体;(2)马来酰亚胺双键与含NH2-,-NH-,-OH,-SH等活性氢的化合物经Michael反应共聚,与苯并环丁烯、桐油等亲二烯体经Diels-Alder反应共聚,与烯丙基类化合物经“ene”反应共聚,与乙烯基单体共聚;(3)与环氧树脂、酚醛树脂进行共混改性。各种改性品种,已在航空航天、机械、电子、电机电器、国防等工业部门得到广泛应用,正迅速发展中。
CAS号:
性质:又称聚顺丁二酰亚胺或双马型聚酰亚胺。由双马来酰亚胺中间体制备的聚合物,是加成型聚酰亚胺中一类重要品种。由顺丁烯二酸酐与二元胺在二甲基甲酰胺或丙酮中反应,然后经脱水和化学酰亚胺化,形成双马来酰亚胺中间体(BMI),再经加成聚合反应形成交联结构的聚双马来酰亚胺。中间体溶于二甲基甲酰胺等强极性溶剂,熔融黏度低,固化过程中无低分子物释放,适宜作耐高温结构胶黏剂、绝缘浸渍漆、模塑料,尤其适用作高性能复合材料基体树脂。均聚物的玻璃化温度大于300℃,可在180~230℃长期使用,因性脆限制了应用。改性的方法很多:(1)合成不同组成或结构的二元胺以及氨基封端的芳醚砜、芳醚酮、有机硅、酰胺-酰亚胺或介晶单元的预聚物,制备相应的双马来酰亚胺中间体;(2)马来酰亚胺双键与含NH2-,-NH-,-OH,-SH等活性氢的化合物经Michael反应共聚,与苯并环丁烯、桐油等亲二烯体经Diels-Alder反应共聚,与烯丙基类化合物经“ene”反应共聚,与乙烯基单体共聚;(3)与环氧树脂、酚醛树脂进行共混改性。各种改性品种,已在航空航天、机械、电子、电机电器、国防等工业部门得到广泛应用,正迅速发展中。