1) delay hydrogen brittleness
延迟氢脆
1.
It is characteristic of delay hydrogen brittleness.
本文应用光学显微镜和扫描电子显微镜(SEM)仔细分析研究了Cr_5Mo法兰焊缝开裂的原因,具有延迟氢脆的特征。
2) delayed brittle fracture
延迟脆断
1.
Studies on cause to the delayed brittle fracture of reinforcing steel barfor pipe peg use;
管桩钢筋延迟脆断的原因研究
3) hydrogen releasing
延迟释氢
4) brittle delay fracture
脆性延迟断裂
1.
This paper analyzes and compares the ends of the brittle delay fracture and hydrogen brittleness of Austenitic alloy, and reveals their difference and relation.
通过对奥氏体合金脆性延迟断裂和氢脆断口的分析和比较，揭示了它们之间的区别和联系，提出了奥氏体合金应力腐蚀断裂与氢脆的机理。
5) hydrogen embrittlement crack
氢致延迟裂纹
1.
The results show that tiny crack main by using the unqualified protect gas(Ar)during welding could cause the increasing hydrogen contain in the weld area,created the hydrogen embrittlement crack.
7倍,在焊缝热影响区造成增氢,导致氢致延迟裂纹的产生。
6) delayed hydride cracking
氢致延迟开裂
1.
The purpose of the present study was to investigate critical temperature for initiating and arresting delayed hydride cracking in Zr-Sn-Nb alloy.
1Cr)发生氢致延迟开裂(DHC)临界最大开裂温度(T_c)和临界最小止裂温度(T_h)随氢含量的变化规律;同时对裂纹尖端偏聚氢含量及静水应力和发生DHC的临界氢含量进行了理论分析,建立理论模型对临界温度进行理论计算。
补充资料：脆脆小黑豆
脆脆小黑豆
材料：绿心黑豆，盐，糖，肉桂粉
做法：超级简单哦~~把绿心黑豆泡水4个小时，等豆豆胀大，沥干水分，放到小盒子里，加入盐，糖，肉桂粉，然后盖上盖子，甩甩甩，摇摇摇，让味道均匀裹在豆豆表面，接着，把豆豆平铺在盘子里，放到微波炉中，中火开5分钟后拿出，搅拌下，再平铺开，放入微波炉中，中火开3分钟后取出，放凉即可。
小贴士：
豆豆放到盘子当中一定要平铺，不然容易焦掉，而且烤的程度不均匀。
也可以把绿心黑豆换成去皮花生之类的~~黄豆我也试过，不过奇怪的是没有黑豆那么脆，有点软。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。