1) wide cold bending
宽冷弯
1.
The main influence factors on wide cold bending performance of 16MnL steel plate for automobile girder are analyzedThe reasonable control measures are put forward for chemical composition of C?Mn and S,banded structure and finishing rolling temperature
分析了影响16MnL汽车大梁板宽冷弯性能的主要因素,对钢中碳、锰、硫含量的控制及带状组织、终轧温度的控制提出了合理的调整范围。
2.
The wide cold bending properties of 16MnL steel by way of metallog raphic and mechanical test are analysed.
通过金相和力学试验方法分析了 16MnL钢中的宽冷弯性能存在的问题。
2) cold bending
冷弯
1.
Analysis of microcrack formation on container plate in cold bending test
集装箱板冷弯裂纹形成分析
2.
The cold bending property is one of the important targets for the hot rolled strip,the cold bending test is required inspection item stipulated in the standards.
冷弯性能是热轧中薄板带材的重要指标之一,冷弯试验是标准规定的必检项目,但在实际生产中经常出现冷弯不合格现象。
3.
The cold-bended crack in the hot rolled plate Q345 can be eliminated by adoption of heating-cold bending process as well as improvement of the c.
利用金相显微镜、X射线衍射仪及电子探针等对Q345热轧钢板因冷弯产生的裂纹进行了系统检验分析。
3) cold-formed
冷弯
1.
Special buckling modes of cold-formed thin-walled flexural members;
冷弯薄壁型钢受弯构件特有的失稳模式
2.
Interaction of local buckling in cold-formed members and effective width of edge-stiffened elements;
冷弯型钢局部屈曲的相关性和卷边板件的有效宽度
3.
Cold-formed thin-walled beams with open cross-sections are widely used in different branches of industry.
开口截面的冷弯薄壁钢梁在工业建筑中被广泛应用。
4) Cold bend
冷弯
1.
The phenomenon that BM510L beam steel plate was crazed in cold bending.
针对BM510L汽车大梁钢板冷弯开裂现象,对纵向和横向试样分别用金相显微镜观察抛光态夹杂物及金相组织,发现断口处夹杂物及带状组织较严重。
2.
In accordance with the requirement of technical parameter of super high pressure bend and cold bend specification, the stress at cold bending on the three-roll bend machine was analyzed.
根据超高压弯管技术参数和冷弯工艺的要求,结合超高压管在立式三辊滚弯机上冷弯时的受力状 态,运用弹塑性理论分析计算出弯管所用弯矩及弯管的最大压紧力,并据此选用弯管设备,解决了超高压弯管的制 造问题。
3.
Some methods of reducing the nonmetallic inclusion and inclusion modification to reduce cracking sensibility during cold bending are proposed.
分析了中厚板试样裂纹处的表层和芯部的夹杂物种类、形状、尺寸、分布以及表层、1/ 4处、芯部的组织 ,确定钢板中的硅酸盐夹杂偏多是冷弯试样出现裂纹的主要原因 ,并指出减少钢液中的非金属夹杂物以及改变夹杂物分布形态是改善试样冷弯性能的有效措
5) cold elbow
冷弯弯头
6) cold bending angle pipe
冷弯弯管
1.
The article introduces city gas common specification cold bending angle pipe angle range selection.
冷弯弯管是燃气输送管道在平面走向改变及竖向变化处所采用的方式之一。