1) polycarbonate polyurethane elastomer
聚碳酸酯型聚氨酯弹性体
1.
A series of aliphatic polycarbonate polyurethane elastomer had been synthesized from methylene diphenyl diisocyanate(MDI) and poly(ethylene ether carbonate) diol which obtained by the copolymerization of ethylene oxide and CO2 in the presence of polymer supported bimetallic catalyst(PBM).
采用以CO2和环氧乙烷在高分子负载双金属氰化物的催化下通过调节聚合得到的聚碳酸亚乙酯多元醇和改性二苯基甲烷二异氰酸酯为主原料,合成了一系列脂肪族聚碳酸酯型聚氨酯弹性体新材料;研究了异氰酸酯指数以及弹性体制备工艺条件对材料力学性能的影响;同时研究了该类新材料的耐溶剂性及生物降解性。
2) polycarbonate polyurethane
聚碳酸酯型聚氨酯
1.
A series of polycarbonate polyurethane(PCU) were prepared with poly(hexamethylene carbonate) diol as soft segment,trimethylol propane and isophorone diisocyanatet as hard segment.
采用溶液预聚法合成了以聚1,6-己二醇碳酸酯二醇(PHMCD)为软段、异佛尔酮二异氰酸酯(IPDI)和三羟甲基丙烷(TMP)为硬段的聚碳酸酯型聚氨酯(PCU),研究了原料配比对PCU性能的影响,利用红外光谱(FT-IR)等对PCU的结构进行了表征,测试了其力学性能和形状记忆性能。
2.
The developmental trends of polycarbonate diols and polycarbonate polyurethane was summarized.
本文论述了聚碳酸酯二元醇及聚碳酸酯型聚氨酯材料的发展概况 ,并分别简述了聚碳酸酯二元醇的合成方法、应用及聚碳酸酯型聚氨酯材料的性能与特
3.
A series of linear polycarbonate polyurethanes (PCUs) with variation of NCO/OH molar ratio and hard segment content was synthesized by solution two-step polymerization, using dibutyltin dilaurate (DBTDL) as catalyst.
随着现代医学的发展,新的医学材料的出现,对生物材料要求越来越高,而聚碳酸酯型聚氨酯材料正是这样一种对生物稳定性、对人体安全很有应用前景的植入材料。
3) polycarbonate urethane
聚碳酸酯聚氨酯
1.
Structure and performance of polycarbonate urethane;
聚碳酸酯聚氨酯的结构及性能
2.
Construction and characterization of a novel sulfoammonium zwitterionic structure onto surface of polycarbonate urethane film;
聚碳酸酯聚氨酯膜表面构建新型磺铵两性结构及其表征
3.
In order to improve the blood-compatibility of polycarbonate urethane (PCU), the surface of PCU film was forced to generate and release endogenous NO via blending with Cu(II)-complex and grafting endogenous NO donors.
为了提高聚碳酸酯聚氨酯(PCU)的血液相容性,本文通过共混和接枝的方法,使聚碳酸酯聚氨酯膜表面能释放内源性NO,以此来提高材料的抗凝血性。
4) polycarbonate urethanes
聚碳酸酯聚氨酯
1.
In the present work, three kinds of polycarbonate urethanes (PCUs) having 40%(mass%) MDI/BDO hard segments were synthesized from poly (tetramethylene carbonate) diol(PBC), poly(hexamethylene carbonate) diol(PHC) and poly(hexamethylene-co-pentamethylene carbonate) diol (PHPC,the molar ratio of hexamethylene and pentamethylene units are 3∶2),respectively, by bulk one-shot method.
采用了聚碳酸 1,4 -丁二醇酯 ( PBC)、聚碳酸 1,6-己二醇酯 ( PHC)和聚碳酸 1,5 -戊二醇 - 1,6-己二醇酯 ( PHPC,其中己二醇链节与戊二醇链节之比为 3∶ 2 )软段 ,4 ,4′-二苯基甲烷二异氰酸酯 / 1,4 -丁二醇 ( MDI/ BDO)为硬段 (其质量含量为 4 0 % )合成出了一系列的聚碳酸酯聚氨酯 ( PCU)弹性体。
5) polycarbonate-polyurethane
聚碳酸酯聚氨酯
1.
In order to study the structure and properties of polycarbonate-polyurethane (PCU), it was synthesized by two different methods and followed by surface modification.
为了研究聚碳酸酯聚氨酯的结构与性能,本文用两种方法合成了聚碳酸酯聚氨酯,对其进行了表面改性,并用多种方法进行表征。
6) CPUE
浇注型聚氨酯弹性体
1.
Study on Shrinkage of BIG CPUE Product;
大型浇注型聚氨酯弹性体制品收缩率的研究
2.
Simulation on rule of shrinkage of large CPUE based on neu ral network;
基于人工神经网络的大型浇注型聚氨酯弹性体收缩规律的模拟
3.
Casting polyurethane elastomer (CPUE ) is commonly called as liquid rubber.
浇注型聚氨酯弹性体(CPUE)俗称液体橡胶,它可以在很高的硬度下保持弹性、优良的耐磨性和良好的机械强度,具有化学稳定性、身体适应性和血液相容性等性质,而且,可流动性好,可以制成几何形状复杂的制品。
补充资料：聚碳酸酯/聚对苯二甲酸丁二酯/弹性体共混物
分子式：
CAS号：
性质： 具有优异的耐化学腐蚀性和一系列优异物理机械性能，在广泛温度范围内有很高的冲击强度，缺口冲击强度为160～860J/m2，弯曲模量高达1.6～2.9GPa；在高低温和潮湿状态下尺寸稳定；耐候性好；成型加工适应性强；有的在-40℃下有更优异的冲击强度，且对缺口半径不敏感；模塑收缩率低；加工流动性好，能制造形状复杂的制件。同时，内应力小，且有优异的耐化学腐蚀性。采用机械共混法制备。适用于制造汽车保险杠、挡泥板、车门和其他大型车内装饰件等；接插件等电器制品；气动或电动割草机甲板等。可与RIM聚氨酯、超韧尼龙等媲美。
CAS号：
性质： 具有优异的耐化学腐蚀性和一系列优异物理机械性能，在广泛温度范围内有很高的冲击强度，缺口冲击强度为160～860J/m2，弯曲模量高达1.6～2.9GPa；在高低温和潮湿状态下尺寸稳定；耐候性好；成型加工适应性强；有的在-40℃下有更优异的冲击强度，且对缺口半径不敏感；模塑收缩率低；加工流动性好，能制造形状复杂的制件。同时，内应力小，且有优异的耐化学腐蚀性。采用机械共混法制备。适用于制造汽车保险杠、挡泥板、车门和其他大型车内装饰件等；接插件等电器制品；气动或电动割草机甲板等。可与RIM聚氨酯、超韧尼龙等媲美。