1)  glazed tile production
釉面砖生产
1.
A technology to treat the wastewater from the glazed tile production by coagulation is presented.
本文提出了以药剂混凝的物理化学方法对陶瓷二分厂釉面砖生产废水的处理工艺。
2)  glazed tile
釉面砖
1.
Glazed tile of good quality has been developed by utilizing waste-flyash as major raw material,as well as minor ceramic materials.
以粉煤灰为主要原料,以其他硅酸盐原料为辅助原料,试制出性能优良的陶瓷釉面砖。
2.
In this research, optimum formulas for the body and glaze of once fast-fired glazed tile was obtained by making reference to their empirical recipes, conducting orthogonal experiments, using analytic instruments like SEM, rationalizing the choice of raw materials and adjusting the mol ratios of Al2O3, K2O and Na2O.
本研究参照经验配方,采用正交实验设计等实验方法,利用扫描电镜等现代分析手段,通过合理选择原料,在配方中调整SiO2、Al_2O_3、K_2O、Na_2O之间的摩尔比,确定了一次烧成釉面砖坯釉的最佳配方,在烧成中采用“阶梯式升温”与快、缓升温结合,对釉面质量起到了促进作用。
3.
on the properties of the glazed tile were analyzed, and then the optimal flyash content in the batch and production process were determined.
以粉煤灰为主要原料,以其它硅酸盐原料做辅助料,试制出性能优良的陶瓷釉面砖。
3)  glazed ceramic tiles
釉面砖
1.
Using a silver compound as a composition of the glaze, the study has prepared one_time fast_firing glazed ceramic tiles with an antibacterial function at low temperatures.
通过在釉中引入银系无机抗菌剂,研制了低温一次快烧的具有抗菌功能的陶瓷釉面砖。
2.
According to the analysis and research on the properties of local calcic clay and waste sulphoslag, batching of body onglazed ceramic tiles is designed by cross experimental design.
对钙质粘土及废弃的硫酸尾渣的性能进行分析研究的基础上,采用正交原理优化设计出釉面砖坯料配方,再配以高强乳 浊釉对其有效遮盖,经生产实际运行,产品指标均达到企业标准要求,为地产原料的研发和废弃尾渣的利用提供了一定 的研究基础。
4)  Facing glazed brick
贴釉面砖
5)  tile body
釉面砖坯
1.
However,the new minerals such as mullite and cristobalite form at a lower temperature in pyrophyllitie tile than in pyrophyllite tile body due to the existence of K_2O-bcaring illitc and other impur.
利用x射线衍射分析对叶蜡石及蜡石质釉面砖坯在不同温度下焙烧的物相变化进行了研究。
6)  salt,glazed tile
盐釉面砖
补充资料:釉面砖
分子式:
CAS号:

性质:内墙装饰用薄片精陶建筑材料。可分为正方形、矩形、异形配件砖等品种。按其组成可分为:硅灰石质、叶蜡石质、瓷石质、石灰石质及长石质等。其化学成分一般为:SiO2 60%~70%,A12O3 15%~22%,CaO 1.0%~10%,MgO 1.0%~3.0%,R2O小于1.0%。吸水率不大于22%。白度不小于78%。耐急冷急热性150℃,一次不裂。耐蚀性好。常用半干压法成型。可分为生坯施釉一次烧成或坯体素烧后施釉入窑釉烧的二次烧成法。前者要求高,质量常不及后者。适用于建筑物的内部装饰。也有作为耐酸槽用。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。