1) reclaimed sand mixture
混合再生砂
3) No-fines pervious recycled concrete
无砂透水再生混凝土
1.
No-fines pervious recycled concrete (NPRC), made from recycled aggregate,cement, water and other materials, is a new kind of concrete with continuous pores,suitable strength and preferable water permeability.
无砂透水再生混凝土是由再生骨料、水泥、水等材料经特殊工艺制成的具有连续孔隙的混凝土,既有一定的强度,又有良好的透气透水性。
4) Recycle asphalt mixture
再生沥青混合料
1.
Finally the proper doses of recycling agent in recycle asphalt mixture are determined.
最后确定出再生沥青混合料的再生剂用量。
5) needed component parts of construction equipment
再生混合料性能
1.
Simply the recycling technique,the mix design,the performance of mixtures,the needed component parts of construction equipment and quality control,etc are presented including different recycling and r.
结合笔者在日本的研究成果,就沥青砼路面的不同再生利用技术中所涉及到的再生工艺、再生混合料配合比设计、再生混合料性能、施工设备配套和质量控制等技术问题作简要介绍。
6) recycled asphalt mixture
再生沥青混合料
1.
Taking plant-mix heat recycle technology as an object of study,key technologies such as the evaluation of waste asphalt material performance,the proportioning ratio design of recycled asphalt mixture and processing etc are studied.
以厂拌热再生技术为研究对象,对废旧沥青混合料性能指标评价、再生混合料配合比设计及生产工艺等关键技术进行了研究,通过试验分析表明:再生沥青混合料具有良好的路用性能,各项检测指标均符合规范要求。
2.
The optimum as- phalt content of recycled asphalt mixture by Marshall is obtainted.
对回收沥青混合料与回收沥青进行了试验分析,并且采用马歇尔试验方法确定了再生沥青混合料的最佳用油量。
补充资料：再生砂
铸造生产中经过处理基本上恢复了使用性能可以回用的旧砂。砂型铸造时，每生产1吨铸件就会产生6～15吨用过的旧砂。旧砂的利用基本上有两种方式，即旧砂回用和旧砂再生。铸型在浇注以后，如果大部分型砂中的粘结剂没有发生不可逆的变化，则只要除掉杂质，经过吸灰冷却和重新混制就可恢复型砂原有的性能，这种处理方式称为旧砂回用，一般只有粘土粘结的型砂才能回用。用化学方式硬化的砂型及型芯（如用油砂、水玻璃砂和各种树脂砂制成的砂型及型芯），其粘结剂的硬化反应是不可逆的，这种情况下的旧砂不能简单地回用，需要把砂粒表面已失效的粘结剂膜脱除，使其基本上恢复原砂的性能，这种处理方式称为旧砂再生。粘土砂型中贴近铸件表面的型砂，经高温作用后粘土变成了死粘土，不能再恢复粘结能力。这样的粘土砂也须经再生处理才能回用。旧砂再生有湿法、干法和热法 3种方法。湿法再生对于粘结剂膜能溶于水的旧砂比较有效，一般用于水玻璃砂。采用这种方法时设备庞大复杂，而且再生后的砂子需要干燥冷却，耗能多，效率低，废水排放量大。干法再生适用于粘结剂膜比较脆的旧砂，设备较简单，多用于再生树脂砂和粘土砂。热法再生须将旧砂加热到800℃以上，将失效的粘结剂烧掉,对于无机粘结剂效果很差，较适用于树脂砂。这种方法耗能多，设备费用高，除壳型砂外一般很少采用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。