1) low temperature hot-press sintering
低温热压烧结
2) low temperature and super high pressure sintering
低温超高压烧结
3) low-temperature nonpressurized sintering
低温无压烧结
1.
High-purity Er2O3 ceramic target material of about 90% relative density was prepared by low-temperature nonpressurized sintering at 1 450 ℃ and with Er2O3nanopowders as its raw material.
以纳米Er2O3粉为原料,通过1 450℃低温无压烧结,成功制取了相对密度为近90%的高纯Er2O3陶瓷靶材。
4) low temperature sintering
低温烧结
1.
In situ synthesis of Al matrix composite reinforced with micron-Al_2O_3 particles by low temperature sintering;
低温烧结原位合成微米级Al_2O_3颗粒强化Al基复合材料
2.
The effects of SiO2 on the properties of low temperature sintering lead antimony-manganese zirconate titanate Pb(Mn1/3Sb2/3)0.
探讨了低温烧结时SiO2掺杂对锑锰锆钛酸铅Pb(Mn1/3Sb2/3)0。
3.
The low temperature sintering technology of boron carbide ceramics is summarized, stating granularity.
综述了各种碳化硼陶瓷低温烧结技术及其影响因素,阐述了粉末粒度、制备工艺和化学成分等关键因素对碳化硼陶瓷烧结温度的影响,分析了进一步降低碳化硼陶瓷烧结温度的可能途径。
5) Low-temperature sintering
低温烧结
1.
Research on low-temperature sintering of AlN ceramics;
氮化铝陶瓷的低温烧结研究
2.
Effect of combined additives on low-temperature sintering of AlN ceramics;
复合助剂对氮化铝陶瓷低温烧结的影响
3.
The application of low-temperature sintering technology to the 90/105m~2 sintering machine of Angang;
低温烧结在安钢90/105m~2烧结机上的应用
补充资料：热压烧结
分子式：
CAS号：
性质：对较难烧结的粉料或生坯在模具内加压加热烧结的方法。加热方式有电阻直接加热，电阻间接加热，感应间接加热，感应直接加热等四种。热压烧结用模具材料主要有石墨，氧化铝和碳化硅等。石墨模具可承受70MPa压力、1500～2500℃的温度。氧化铝模具可承受200MPa压力、约1200℃的温度。加压操作方式有：（1）恒压法，整个升温过程中都施加预定的压力；（2）高温加压法：高温阶段才加压；（3）分段加压法，低温时加低压、高温时加到预定的压力。此外还可分为真空热压烧结、气氛热压烧结、连续加压烧结、超高压烧结和超高温超高压烧结等。采用热压烧结可以制造高强度、高密度、高透明度的陶瓷制品。
CAS号：
性质：对较难烧结的粉料或生坯在模具内加压加热烧结的方法。加热方式有电阻直接加热，电阻间接加热，感应间接加热，感应直接加热等四种。热压烧结用模具材料主要有石墨，氧化铝和碳化硅等。石墨模具可承受70MPa压力、1500～2500℃的温度。氧化铝模具可承受200MPa压力、约1200℃的温度。加压操作方式有：（1）恒压法，整个升温过程中都施加预定的压力；（2）高温加压法：高温阶段才加压；（3）分段加压法，低温时加低压、高温时加到预定的压力。此外还可分为真空热压烧结、气氛热压烧结、连续加压烧结、超高压烧结和超高温超高压烧结等。采用热压烧结可以制造高强度、高密度、高透明度的陶瓷制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。